PTFE Sheet: Compact-Extruded Films, Sintered, Laid at 45° and Fused (MacFarland, Hills-McCanna, US 3,130,954)
Thick PTFE was cut from a sintered billet with a knife, and the skived sheet tore along the knife marks. MacFarland built his sheet up instead, from thin extruded films laid crosswise and fused together, for the liner of a valve diaphragm.
Result: a dense PTFE sheet, about 7,000 psi tensile and 450 % elongation, much the same in every direction.
Source: MacFarland, US 3,130,954 (Hills-McCanna, 1964). Not given: furnace temperature, mill pressure. Picture drawn by Youblob.
上級者
Factory process
手順
1
1
Compact-extrude a film
Compact-extrude a film
Feed finely divided PTFE resin from a hopper through a screw extruder to a slot die, usually without added heat. It comes out as a compact film that holds together unsintered, up to 24 in wide.
このステップの材料:
PTFE 樹脂粉末1 as required必要な工具:
プラスチック押出機
押出ダイ2
2
Sinter and coin the film
Sinter and coin the film
Carry the film through a sintering furnace to its fusion (gel) state and coin it in a mill as it goes. It comes out dense, with few pores, 5-8 mils thick. Ours: muffle furnace and calender rolls.
必要な工具:
マッフル炉
平滑カレンダーロール3
3
Lay the films crosswise and fuse them
Lay the films crosswise and fuse them
Each film is a little stronger lengthwise, so stack several with their lengthwise axes turned by the same angle each time; 45° works well (MacFarland shows five plies). Feed the stack into a final sintering and compacting mill to fuse it into one sheet (over 20 mils thick). Ours: muffle furnace and calender rolls.
必要な工具:
マッフル炉平滑カレンダーロールこの設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。