Samarium: Oxide Reduced with Graphite at 1700 °C in Vacuum and Distilled Twice (Downing, Gorski and Koerner, US 3,104,970)
Samarium holds on to oxygen too hard for ordinary smelting. Heated with graphite in a hard vacuum it boils off as samarium carbide vapour; a second distillation of that carbide, caught on a tantalum plate, gives the metal itself.
Result: samarium metal, 99.7 % pure.
Source: J. H. Downing, H. L. Gorski and E. L. Koerner, US 3,104,970 (1963), Example I. Work at 1700 °C under vacuum. Picture drawn by Youblob.
上級者
1 day
手順
1
1
Mix and pellet
Mix and pellet
Mix intimately 79 parts by weight of 99.9 % samarium oxide with 21 parts of powdered graphite (12.7 % more carbon than the oxygen needs), with no particle larger than about 50 microns. Press into pellets 0.75 in across; pellets let the gases and vapour escape.
このステップの材料:
酸化サマリウム1 79 parts by weight必要な工具:
黒鉛粉末
油圧プレス2
2
Reduce and distil to carbide
Reduce and distil to carbide
Heat the pellets in a vacuum induction furnace to 1700 °C under 0.5 micron or less and hold three hours. Samarium carbide condenses on a graphite condenser (carbon resists the carbon monoxide given off). Only a little oxide and carbon stay behind; they can go back into the next charge.
必要な工具:
黒鉛るつぼ
誘導炉
真空ポンプ
黒鉛凝縮器3
3
Distil the metal onto tantalum
Distil the metal onto tantalum
Heat the carbide from the first condenser to 1700 °C under 0.05 micron and hold two hours. Samarium metal condenses on a tantalum condenser: 99.7 % samarium, 0.05 % carbon, 0.10 % oxygen.
必要な工具:
黒鉛るつぼ誘導炉真空ポンプ
タンタル凝縮器この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。