Strontium Ferrite Disc Magnet, Sintered 4 Hours at 1300 °C (Went, Philips 1956, Ex. 34)
A strontium ferrite magnet made exactly like Went's barium ferrite of Example 34, with strontium carbonate in place of barium carbonate: 29.5 g of it to 191.7 g iron oxide, milled, fired, milled again, pressed and sintered for 4 hours. This iteration sinters at 1300 °C, where his rod held 1,850 gauss with a coercive force of 2,130 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 34. They pressed rods; the disc size is ours. The patent does not say how to magnetise it; our way is stated. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
上級者
2 days
手順
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 29.5 g of strontium carbonate and 191.7 g of ferric oxide, Fe2O3. The patent makes this second mixture "in exactly the same manner" as the barium one.
このステップの材料:
炭酸ストロンチウム29.5 g
酸化第二鉄191.7 g必要な工具:
天秤ばかり
ゴム手袋
P100 防じんマスク2
2
Mill with ethanol for 4 hours
Mill with ethanol for 4 hours
Grind the mixture with ethanol in an iron ball mill for 4 hours. Let the ethanol evaporate, then dry the powder in a drying oven.
必要な工具:
鉄製ボールミル
エタノール——試薬級、95 %
乾燥炉3
3
Presinter at 1000 °C for 4 hours
Presinter at 1000 °C for 4 hours
Fire the dry powder in air at 1000 °C for 4 hours (ours: in a lidded porcelain crucible in a muffle furnace). Let it cool.
必要な工具:
マッフル炉
蓋付きるつぼ（磁製）
るつぼばさみ
耐熱手袋4
4
Mill again for 4 hours
Mill again for 4 hours
Grind the presintered product with ethanol in the ball mill for another 4 hours. Let the ethanol evaporate.
必要な工具:
鉄製ボールミルエタノール——試薬級、95 %乾燥炉P100 防じんマスク5
5
Press discs at 1.5 tons per cm²
Press discs at 1.5 tons per cm²
Press the powder at 1.5 tons/cm². The patent pressed rods; we press discs. Ours: a die 20 mm across, so about 4.7 tonnes on the punch (our arithmetic: 1.5 × 3.14 cm²).
必要な工具:
油圧プレス
円板プレス金型6
6
Sinter 4 hours at 1300 °C
Sinter 4 hours at 1300 °C
Sinter the discs for 4 hours at 1300 °C in oxygen or in air. The patent's strontium rod at 1300 °C: 1,850 gauss and 2,130 oersted.
必要な工具:
マッフル炉るつぼばさみ耐熱手袋7
7
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
必要な工具:
電磁石
方位磁針この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)
Charlie 作
産業用
11
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)
Charlie 作
産業用
14
0
0
0
0
0
危険
Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Charlie 作
産業用
17
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated
Charlie 作
無機
12
0
0
0
0
0
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。