Violet Iron Oxide: Precipitated Hematite Calcined at 1000-1100 °C (Nurdini et al. 2022)
Iron hydroxide is thrown down from hot ferric nitrate solution with ammonia, washed, dried and calcined. All of it ends as pure hematite, but the colour moves from bright red through dark red to purple as the calcining heat rises from 1000 °C, because the grains grow larger and more crystalline.
Result: pure violet to purple ferric oxide (hematite) after 4 hours at 1000-1100 °C.
Source: Nurdini et al., Heliyon 8 (2022) e10377, sections 2.2 and 4. Not given: batch size, how much ammonia, end pH, yield. Picture drawn by Youblob.
中級者
2 days
手順
1
1
Heat the ferric nitrate solution
Heat the ferric nitrate solution
Make a 0.05 M solution of ferric nitrate in distilled water and heat it to 80 °C.
このステップの材料:
硝酸鉄(III)1 as required必要な工具:
蒸留水
ガラスビーカー
ホットプレート
温度計2
2
Throw down the hydroxide with ammonia
Throw down the hydroxide with ammonia
Keeping it at 80 °C, add ammonia solution drop by drop while stirring well. Stir for 3 hours, then let it cool to room temperature: a red-brown precipitate forms. Not given: how much ammonia.
必要な工具:
アンモニア水 25-28 %
滴下漏斗ホットプレート温度計3
3
Spin down, wash and dry
Spin down, wash and dry
Collect the precipitate in a centrifuge at 4000 rpm for 15 minutes, wash it with distilled water, and dry it at 110 °C for 24 hours.
必要な工具:
卓上遠心機蒸留水
乾燥炉4
4
Calcine at 1000-1100 °C
Calcine at 1000-1100 °C
Calcine for 4 hours in air at 1000-1100 °C. Below 1000 °C it stays bright or dark red; from 1000 °C it turns purple. Grind the cooled oxide to a fine powder (they used an agate mortar).
必要な工具:
マッフル炉
乳鉢と乳棒この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。