Metal Oxide Varistor: Zinc Oxide with Manganese and Antimony Oxides, Bismuth Paste Fired On (Masuyama 1972, Ex. 6)
A varistor with manganese dioxide and antimony trioxide mixed into the zinc oxide, and bismuth oxide fired on from a paste: 99.0 % zinc oxide, 0.5 % manganese dioxide and 0.5 % antimony trioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 190 at 1 mA and a nonlinearity exponent n of 34.5.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 6. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
上級者
2 days
手順
1
1
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, manganese dioxide and antimony trioxide 99 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.771 g zinc oxide, 0.053 g manganese dioxide, 0.177 g antimony trioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
このステップの材料:
酸化亜鉛粉末9.771 g
二酸化マンガン（軟マンガン鉱）0.053 g
三酸化アンチモン0.177 g必要な工具:
天秤ばかり
鉄製ボールミル
乾燥炉2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
必要な工具:
油圧プレス
円板プレス金型
ノギス3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
必要な工具:
マッフル炉4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 6 gives no thickness.
必要な工具:
炭化ケイ素砥粒ノギス5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
このステップの材料:
酸化ビスマス1 as required必要な工具:
エポキシ樹脂
n-ブタノールマッフル炉6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
このステップの材料:
アルミインゴット1 as 3.2 mm spray wire
銀導電塗料1 as required
銅線2 個必要な工具:
ノギス
アーク溶射ガン
産業用空気圧縮機材料
7- 9.771 gプレースホルダー
- 0.053 gプレースホルダー
- 0.177 gプレースホルダー
- 1 as requiredプレースホルダー
- 1 as 3.2 mm spray wireプレースホルダー
- 1 as requiredプレースホルダー
- 2 個プレースホルダー
この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
Metal Oxide Varistor: Zinc Oxide with 0.2 % Bismuth Oxide, Sintered Disc (Masuyama 1972)
Ed 作
産業用
5
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide with 0.2 % Manganese Dioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
Ed 作
産業用
5
0
0
0
0
0
Antimony Trioxide: Roasted Antimony Fused with More Metal (Thorpe 1912)
Charlie 作
産業用
14
0
0
0
0
0
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。