Metal Oxide Varistor: Zinc Oxide with Bismuth and Manganese Oxides, 1350 °C (Masuyama 1972)
Masuyama, Matsuoka and Nishi found that adding a second oxide to zinc oxide and bismuth oxide changes the varistor a great deal. This is their Example 2 with manganese dioxide: 99.0 % zinc oxide, 0.5 % bismuth oxide and 0.5 % manganese dioxide by moles, sintered at 1350 °C. The disc measured a C-value of 84 at 1 mA and a nonlinearity exponent n of 14.6.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 2. Unknown: what the silver paint is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
上級者
1 day
手順
1
1
Weigh 99.0 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99.0 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide and manganese dioxide 99.0 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.668 g zinc oxide, 0.28 g bismuth oxide, 0.052 g manganese dioxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
このステップの材料:
酸化亜鉛粉末9.668 g
酸化ビスマス0.28 g
二酸化マンガン（軟マンガン鉱）0.052 g必要な工具:
天秤ばかり
鉄製ボールミル
乾燥炉2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
必要な工具:
油圧プレス
円板プレス金型
ノギス3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air at 1350 °C for 1 hour, then let them cool in the furnace to room temperature (about 15-30 °C).
必要な工具:
マッフル炉4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
必要な工具:
炭化ケイ素砥粒ノギス5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
このステップの材料:
アルミインゴット1 as 3.2 mm spray wire
銀導電塗料1 as required
銅線2 個必要な工具:
ノギス
アーク溶射ガン
産業用空気圧縮機材料
6- 9.668 gプレースホルダー
- 0.28 gプレースホルダー
- 0.052 gプレースホルダー
- 1 as 3.2 mm spray wireプレースホルダー
- 1 as requiredプレースホルダー
- 2 個プレースホルダー
この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。