Barium-Strontium Ferrite Disc Magnet: 0.5 mol BaCO3, 0.5 mol SrCO3, 1240 °C (Went, Philips 1956, Ex. 29)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Imeundwa na

Charlie

28. Oktoba 2026DE
1
0
0
0
0

Barium-Strontium Ferrite Disc Magnet: 0.5 mol BaCO3, 0.5 mol SrCO3, 1240 °C (Went, Philips 1956, Ex. 29)

A ceramic magnet with both barium and strontium: 0.5 mol barium carbonate and 0.5 mol strontium carbonate to 2.5 mol iron oxide, milled as in Example 28, pressed and passed through a 1240 °C furnace in 10 minutes. Went's rod held 1,550 gauss with a coercive force of 3,410 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 29. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Juu
2 days

Maagizo

1

Weigh the carbonates and iron oxide

Weigh 99.2 g barium carbonate (0.5 mol), 73.8 g strontium carbonate (0.5 mol), 402.0 g ferric oxide (2.5 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Vifaa kwa hatua hii:

Kabonati ya bariamu (witherite)Kabonati ya bariamu (witherite)99.2 g
Kaboneti ya strontiamuKaboneti ya strontiamu73.8 g
Oksidi ya feriOksidi ya feri402 g

Zana zinazohitajika:

Mizani ya mizani-mbiliMizani ya mizani-mbili
Glavu za mpiraGlavu za mpira
Kinga ya Kupumua ya P100Kinga ya Kupumua ya P100
2

Mill with alcohol 15 hours, dry

As in Example 28: grind the mixture with alcohol in a ball mill for 15 hours, then dry it.

Zana zinazohitajika:

Kinu cha mipira ya chumaKinu cha mipira ya chuma
Etanoli ya maabara, 95 %Etanoli ya maabara, 95 %
Tanuri la kukaushiaTanuri la kukaushia
3

Press the powder

Example 28 moulds a rod without giving the pressure. Ours: press discs at 1.5 tonnes per cm², the pressure of the patent's other examples.

Zana zinazohitajika:

Mashine ya kubana ya haidrolikiMashine ya kubana ya haidroliki
Kalibu ya kubana diskiKalibu ya kubana diski
4

Pass through a 1240 °C zone in 10 minutes

Sinter at 1240 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Zana zinazohitajika:

Tanuru ya MrijaTanuru ya Mrija
Glavu Zinazostahimili JotoGlavu Zinazostahimili Joto
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Zana zinazohitajika:

Sumaku ya umemeSumaku ya umeme
DiraDira

Vifaa

3

Zana Zinazohitajika

12

Mchoro huu unatengeneza

Thumbnail
Kishikilia nafasi

Sumaku ya Diski

Free

2
0
1

Blueprint zinazohusiana

Blueprint hizi zinashiriki maarifa — mbinu, vifaa au kanuni

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

na CharlieDE

Viwandani

2
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

na CharlieDE

Viwandani

6
0
0
0
0
0

CC0 Umma Wote

Mchoro huu umetolewa chini ya CC0. Uko huru kunakili, kubadilisha, kusambaza, na kutumia kazi hii kwa madhumuni yoyote, bila kuomba ruhusa.

Saidia Mtengenezaji kwa kununua bidhaa kupitia Mchoro wao ambapo wanapata Kamisheni ya Mtengenezaji iliyowekwa na Wachuuzi, au unda marudio mapya ya Mchoro huu na uiunganishe kama kiungo katika Mchoro wako kuchangia mapato.

Majadiliano

(0)

Ingia kujiunga na majadiliano

Inapakia maoni...