Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1150 °C, Presintered Twice at 900 °C (Snoek 1948, Ex. I)
A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, presintered twice at 900 °C, pressed into a ring and sintered at 1150 °C in oxygen. Snoek's ring had an initial permeability of 310.
Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. Unknown: the 'violet' iron oxide, linked to an unknown head. Picture: the patent's Fig. 4, the ring core.
Juu
2 days
Maagizo
1
1
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Unknown: what makes the iron oxide 'violet'; Snoek does not say.
Vifaa kwa hatua hii:
Oksidi ya shaba13.24 g
Poda ya oksidi ya zinki20.32 g
Oksidi ya chuma ya zambarau66.44 g
Dioksidi ya manganizi (pairolusiti)1 gZana zinazohitajika:
Mizani ya mizani-mbili
Barakoa ya vumbi2
2
Grind half an hour in an iron ball mill
Grind half an hour in an iron ball mill
Grind the mixture for half an hour in a mill with iron balls.
Zana zinazohitajika:
Kinu cha mipira ya chumaBarakoa ya vumbi3
3
Presinter at 900 °C for 2 hours in oxygen
Presinter at 900 °C for 2 hours in oxygen
Heat the ground powder to 900 °C for 2 hours in oxygen and let it cool.
Zana zinazohitajika:
Tanuru ya Mrija
Oksijeni
Mtungi wa gesi yenye shinikizo
Kipima joto kali
Kikaango cha kuyeyushia chenye mfuniko (kaure)
Glavu Zinazostahimili Joto4
4
Grind and presinter at 900 °C again (2 of 2)
Grind and presinter at 900 °C again (2 of 2)
Grind the powder, then heat it once more to 900 °C in oxygen. Snoek gives no times for the repeats.
Zana zinazohitajika:
Kinu cha mipira ya chumaTanuru ya MrijaOksijeniMtungi wa gesi yenye shinikizoKikaango cha kuyeyushia chenye mfuniko (kaure)Glavu Zinazostahimili JotoBarakoa ya vumbi5
5
Grind 2 hours with iron balls
Grind 2 hours with iron balls
Grind it for 2 hours in a disintegrator with iron balls.
Zana zinazohitajika:
Kinu cha mipira ya chumaBarakoa ya vumbi6
6
Press a ring at 4 tons per cm²
Press a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.
Zana zinazohitajika:
Mashine ya kubana ya haidroliki
Kalibu ya kubonyeza peteBarakoa ya vumbi7
7
Sinter at 1150 °C in oxygen, cool 5–10 °C a minute
Sinter at 1150 °C in oxygen, cool 5–10 °C a minute
Sinter the ring at 1150 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 310, measured at room temperature at 2 kHz.
Zana zinazohitajika:
Tanuru ya MrijaOksijeniMtungi wa gesi yenye shinikizoKipima joto kali
Koleo la kaure ya kuyeyushiaGlavu Zinazostahimili JotoVifaa
4- 13.24 gKishikilia Nafasi
- 20.32 gKishikilia Nafasi
- 66.44 gKishikilia Nafasi
- Kishikilia Nafasi
Zana Zinazohitajika
12- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
Mchoro huu unatengeneza
Blueprint zinazohusiana
Blueprint hizi zinashiriki maarifa — mbinu, vifaa au kanuni
CC0 Umma Wote
Mchoro huu umetolewa chini ya CC0. Uko huru kunakili, kubadilisha, kusambaza, na kutumia kazi hii kwa madhumuni yoyote, bila kuomba ruhusa.
Saidia Mtengenezaji kwa kununua bidhaa kupitia Mchoro wao ambapo wanapata Kamisheni ya Mtengenezaji iliyowekwa na Wachuuzi, au unda marudio mapya ya Mchoro huu na uiunganishe kama kiungo katika Mchoro wako kuchangia mapato.