Lead Ferrite Disc Magnet: 0.15 mol PbO2 to 0.9 mol Iron Oxide, Presintered at 900 °C (Went, Philips 1956, Ex. 17)
A lead ferrite magnet: 0.15 mol lead dioxide to 0.9 mol iron oxide, milled in an iron ball mill, dried at 150 °C, presintered 2 hours at 900 °C, pressed and passed through a 1150 °C furnace in 3 to 5 minutes. Went's rod held 1,420 gauss with a coercive force of 1,830 oersted. Lead compounds are poisonous.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 17. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Juu
2 days
Maudhui hatari
Blueprint hii ina taratibu za hatari. Ingia na uwashe maudhui ya hatari katika mipangilio ya akaunti yako ili kuona maagizo ya hatua kwa hatua.
IngiaMchoro huu unatengeneza
Blueprint zinazohusiana
Blueprint hizi zinashiriki maarifa — mbinu, vifaa au kanuni
CC0 Umma Wote
Mchoro huu umetolewa chini ya CC0. Uko huru kunakili, kubadilisha, kusambaza, na kutumia kazi hii kwa madhumuni yoyote, bila kuomba ruhusa.
Saidia Mtengenezaji kwa kununua bidhaa kupitia Mchoro wao ambapo wanapata Kamisheni ya Mtengenezaji iliyowekwa na Wachuuzi, au unda marudio mapya ya Mchoro huu na uiunganishe kama kiungo katika Mchoro wako kuchangia mapato.