Strontium Ferrite Disc Magnet: 1 mol SrCO3 to 3 mol Iron Oxide, 1220 °C (Went, Philips 1956, Ex. 10)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Imeundwa na

Charlie

28. Oktoba 2026DE
3
0
0
0
0

Strontium Ferrite Disc Magnet: 1 mol SrCO3 to 3 mol Iron Oxide, 1220 °C (Went, Philips 1956, Ex. 10)

A strontium ferrite: 1 mol strontium carbonate to 3 mol iron oxide, milled, bound and formed as in Example 4, and passed through a 1220 °C furnace in 10 minutes. Went's rod held 1,790 gauss with a coercive force of 3,260 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 10. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Juu
2 days

Maagizo

1

Weigh strontium carbonate and iron oxide

Weigh 147.6 g strontium carbonate (1 mol) and 484.1 g ferric oxide (3 mol).

Vifaa kwa hatua hii:

Kaboneti ya strontiamuKaboneti ya strontiamu147.6 g
Oksidi ya feriOksidi ya feri484.1 g

Zana zinazohitajika:

Mizani ya mizani-mbiliMizani ya mizani-mbili
Kinga ya Kupumua ya P100Kinga ya Kupumua ya P100
2

Mill with alcohol 15.5 hours, dry and sieve

As in Example 4: grind the mixture with alcohol in a ball mill for 15.5 hours, then dry it and sieve it.

Zana zinazohitajika:

Kinu cha mipira ya chumaKinu cha mipira ya chuma
Etanoli ya maabara, 95 %Etanoli ya maabara, 95 %
Tanuri la kukaushiaTanuri la kukaushia
UngoUngo
3

Knead with a binder and form

Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.

Zana zinazohitajika:

Unga wa polivinili alkoholiUnga wa polivinili alkoholi
Mashine ya kubana ya haidrolikiMashine ya kubana ya haidroliki
Kalibu ya kubana diskiKalibu ya kubana diski
Tanuri la kukaushiaTanuri la kukaushia
4

Pass through a 1220 °C zone in 10 minutes

Sinter in air at 1220 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Zana zinazohitajika:

Tanuru ya MrijaTanuru ya Mrija
Glavu Zinazostahimili JotoGlavu Zinazostahimili Joto
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Zana zinazohitajika:

Sumaku ya umemeSumaku ya umeme
DiraDira

Vifaa

2

Zana Zinazohitajika

13

Mchoro huu unatengeneza

Thumbnail
Kishikilia nafasi

Sumaku ya Diski

Free

2
0
1

Blueprint zinazohusiana

Blueprint hizi zinashiriki maarifa — mbinu, vifaa au kanuni

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

na CharlieDE

Viwandani

2
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

na CharlieDE

Viwandani

6
0
0
0
0
0

CC0 Umma Wote

Mchoro huu umetolewa chini ya CC0. Uko huru kunakili, kubadilisha, kusambaza, na kutumia kazi hii kwa madhumuni yoyote, bila kuomba ruhusa.

Saidia Mtengenezaji kwa kununua bidhaa kupitia Mchoro wao ambapo wanapata Kamisheni ya Mtengenezaji iliyowekwa na Wachuuzi, au unda marudio mapya ya Mchoro huu na uiunganishe kama kiungo katika Mchoro wako kuchangia mapato.

Majadiliano

(0)

Ingia kujiunga na majadiliano

Inapakia maoni...