Metal Oxide Varistor: Zinc Oxide with Manganese and Chromic Oxides, Bismuth Paste Fired On (Masuyama 1972, Ex. 6)
A varistor with manganese dioxide and chromic oxide mixed into the zinc oxide, and bismuth oxide fired on from a paste: 99.0 % zinc oxide, 0.5 % manganese dioxide and 0.5 % chromic oxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 282 at 1 mA and a nonlinearity exponent n of 25.6.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 6. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Juu
2 days
Maagizo
1
1
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, manganese dioxide and chromic oxide 99 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.854 g zinc oxide, 0.053 g manganese dioxide, 0.093 g chromic oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Vifaa kwa hatua hii:
Poda ya oksidi ya zinki9.854 g
Dioksidi ya manganizi (pairolusiti)0.053 g
Oksidi ya Kromi0.093 gZana zinazohitajika:
Mizani ya mizani-mbili
Kinu cha mipira ya chuma
Tanuri la kukaushia2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Zana zinazohitajika:
Mashine ya kubana ya haidroliki
Kalibu ya kubana diski
Kalipa ya Vernier3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Zana zinazohitajika:
Tanuri ya muffle4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 6 gives no thickness.
Zana zinazohitajika:
Chembechembe za kabidi ya silikoniKalipa ya Vernier5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Vifaa kwa hatua hii:
Oksidi ya bismuthi1 as requiredZana zinazohitajika:
Utomvu wa epoksi
n-ButanolTanuri ya muffle6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Vifaa kwa hatua hii:
Kitalu cha alumini1 as required
Rangi ya fedha inayopitisha umeme1 as required
Waya wa Shaba2 vipandeZana zinazohitajika:
Njia isiyojulikana ya kunyunyizia chumaKalipa ya VernierVifaa
7- 9.854 gKishikilia Nafasi
- Kishikilia Nafasi
- 0.093 gKishikilia Nafasi
- 1 as requiredKishikilia Nafasi
- 1 as requiredKishikilia Nafasi
- 1 as requiredKishikilia Nafasi
- 2 vipandeKishikilia Nafasi
Zana Zinazohitajika
11- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
- Kishikilia Nafasi
Mchoro huu unatengeneza
Blueprint zinazohusiana
Blueprint hizi zinashiriki maarifa — mbinu, vifaa au kanuni
CC0 Umma Wote
Mchoro huu umetolewa chini ya CC0. Uko huru kunakili, kubadilisha, kusambaza, na kutumia kazi hii kwa madhumuni yoyote, bila kuomba ruhusa.
Saidia Mtengenezaji kwa kununua bidhaa kupitia Mchoro wao ambapo wanapata Kamisheni ya Mtengenezaji iliyowekwa na Wachuuzi, au unda marudio mapya ya Mchoro huu na uiunganishe kama kiungo katika Mchoro wako kuchangia mapato.