Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1100 °C (Snoek 1948, Ex. I)

A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, pressed into a ring and sintered at 1100 °C in oxygen. Snoek's ring had an initial permeability of 118. Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. The violet iron oxide has its own blueprint (precipitated hematite calcined at 1000-1100 °C, after Nurdini et al. 2022); Snoek does not say how his was made. Picture: the patent's Fig. 4, the ring core.

고급

2 days

안내

Weigh 20 : 30 : 50 mol % and 1 % brownstone

Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Snoek does not say what makes it 'violet'; violet iron oxide has its own blueprint.

이 단계의 재료:

산화 구리13.24 g

산화아연 분말20.32 g

보라색 산화철66.44 g

이산화망가니즈 (연망가니즈석)1 g

필요한 도구:

접시 저울

방진 마스크

Grind half an hour in an iron ball mill

Grind the mixture for half an hour in a mill with iron balls.

필요한 도구:

철 볼 밀

방진 마스크

Press a ring at 4 tons per cm²

Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.

필요한 도구:

유압 프레스

링 프레스 다이

방진 마스크

Sinter at 1100 °C in oxygen, cool 5–10 °C a minute

Sinter the ring at 1100 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 118, measured at room temperature at 2 kHz.

필요한 도구: