Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. In his first ferrite patent (US 2,452,529, 1948) Snoek at Philips ground the oxides very fine and fired rings in oxygen. This magnesium-zinc ferrite (28 : 18 : 54 mol %) is milled 30 hours and fired 2 hours at 1400 °C; his core had an initial permeability of 150.
The picture: our diagram.
고급
3 days
안내
1
1
Mix 28 : 18 : 54 mol
Mix 28 : 18 : 54 mol
Mix pure magnesium oxide, zinc oxide and ferric oxide, 28 : 18 : 54 mol %. Ours, by weight: 10.06 g magnesium oxide, 13.06 g zinc oxide and 76.88 g ferric oxide per 100 g.
이 단계의 재료:
산화마그네슘10.06 g
산화아연 분말13.06 g
산화제이철76.88 g필요한 도구:
접시 저울
방진 마스크2
2
Grind 30 hours in an iron ball mill
Grind 30 hours in an iron ball mill
Grind the mixture for 30 hours in an iron ball mill.
필요한 도구:
철 볼 밀방진 마스크3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
필요한 도구:
유압 프레스
링 프레스 다이4
4
Fire 2 hours at 1400 °C, cool slowly
Fire 2 hours at 1400 °C, cool slowly
Heat the ring in oxygen for 2 hours at 1400 °C, then cool it slowly in oxygen at 5–10 °C a minute. Snoek's core: initial permeability 150.
필요한 도구:
관상로
산소
고압 가스통
고온계
도가니 집게
내열 장갑이 블루프린트로 만드는 것
관련 블루프린트
이 블루프린트들은 지식을 공유합니다 — 기술, 재료 또는 원리
CC0 퍼블릭 도메인
이 블루프린트는 CC0로 공개되었습니다. 어떤 목적으로든 자유롭게 복사, 수정, 배포 및 사용할 수 있습니다.
제품 구매를 통해 메이커를 지원하세요. 판매자가 설정한 메이커 커미션 을 받거나, 이 블루프린트의 새로운 반복을 만들어 연결로 포함시킬 수 있습니다.