Violet Iron Oxide: Precipitated Hematite Calcined at 1000-1100 °C (Nurdini et al. 2022)
Iron hydroxide is thrown down from hot ferric nitrate solution with ammonia, washed, dried and calcined. All of it ends as pure hematite, but the colour moves from bright red through dark red to purple as the calcining heat rises from 1000 °C, because the grains grow larger and more crystalline.
Result: pure violet to purple ferric oxide (hematite) after 4 hours at 1000-1100 °C.
Source: Nurdini et al., Heliyon 8 (2022) e10377, sections 2.2 and 4. Not given: batch size, how much ammonia, end pH, yield. Picture drawn by Youblob.
중급
2 days
안내
1
1
Heat the ferric nitrate solution
Heat the ferric nitrate solution
Make a 0.05 M solution of ferric nitrate in distilled water and heat it to 80 °C.
이 단계의 재료:
질산철(III)1 as required필요한 도구:
증류수
유리 비커
전열판(핫플레이트)
온도계2
2
Throw down the hydroxide with ammonia
Throw down the hydroxide with ammonia
Keeping it at 80 °C, add ammonia solution drop by drop while stirring well. Stir for 3 hours, then let it cool to room temperature: a red-brown precipitate forms. Not given: how much ammonia.
필요한 도구:
암모니아수 25-28 %
적하 깔때기전열판(핫플레이트)온도계3
3
Spin down, wash and dry
Spin down, wash and dry
Collect the precipitate in a centrifuge at 4000 rpm for 15 minutes, wash it with distilled water, and dry it at 110 °C for 24 hours.
필요한 도구:
탁상 원심분리기증류수
건조 가마4
4
Calcine at 1000-1100 °C
Calcine at 1000-1100 °C
Calcine for 4 hours in air at 1000-1100 °C. Below 1000 °C it stays bright or dark red; from 1000 °C it turns purple. Grind the cooled oxide to a fine powder (they used an agate mortar).
필요한 도구:
머플로
막자사발과 막자이 블루프린트로 만드는 것
관련 블루프린트
이 블루프린트들은 지식을 공유합니다 — 기술, 재료 또는 원리
CC0 퍼블릭 도메인
이 블루프린트는 CC0로 공개되었습니다. 어떤 목적으로든 자유롭게 복사, 수정, 배포 및 사용할 수 있습니다.
제품 구매를 통해 메이커를 지원하세요. 판매자가 설정한 메이커 커미션 을 받거나, 이 블루프린트의 새로운 반복을 만들어 연결로 포함시킬 수 있습니다.