Metal Oxide Varistor: Zinc Oxide with 0.5 % Bismuth Oxide, 1100 °C, 1.0 mm (Masuyama 1972)
A non-linear resistor: the current through it rises far faster than the voltage across it. Masuyama, Matsuoka and Nishi made one from zinc oxide with a little bismuth oxide: pressed into a disc, sintered, lapped, and given metal electrodes. With 0.5 mole % bismuth oxide, sintered at 1100 °C and lapped to 1.0 mm, the disc measured a C-value of 53 at 1 mA and a nonlinearity exponent n of 4.8.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 1. Unknown: what the silver paint is. The patent calls the spraying and the paint well known. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
고급
1 day
안내
1
1
Weigh 99.5 ZnO to 0.5 Bi2O3 and wet-mill 5 hours
Weigh 99.5 ZnO to 0.5 Bi2O3 and wet-mill 5 hours
Mix zinc oxide and bismuth oxide 99.5 : 0.5 by moles. Ours, for 10 g: 9.72 g zinc oxide and 0.28 g bismuth oxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
이 단계의 재료:
산화아연 분말9.72 g
산화 비스무트0.28 g필요한 도구:
접시 저울
철 볼 밀
건조 가마2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm².
필요한 도구:
유압 프레스
원판 압축 금형
버니어 캘리퍼스3
3
Sinter 1 hour at 1100 °C and furnace-cool
Sinter 1 hour at 1100 °C and furnace-cool
Sinter the discs in air for 1 hour at 1100 °C, then let them cool in the furnace to room temperature (about 15-30 °C). Above 1200 °C the disc loses its nonlinearity.
필요한 도구:
머플로4
4
Lap both faces to 1.0 mm
Lap both faces to 1.0 mm
Lap both faces with 600-mesh silicon carbide until the disc is 1.0 mm thick.
필요한 도구:
탄화규소 연마입자버니어 캘리퍼스5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
이 단계의 재료:
알루미늄 잉곳1 as 3.2 mm spray wire
은 도전성 도료1 as required
구리선2 개필요한 도구:
버니어 캘리퍼스
아크 용사 건
산업용 공기 압축기재료
5- 9.72 g플레이스홀더
- 0.28 g플레이스홀더
- 1 as 3.2 mm spray wire플레이스홀더
- 1 as required플레이스홀더
- 2 개플레이스홀더
이 블루프린트로 만드는 것
관련 블루프린트
이 블루프린트들은 지식을 공유합니다 — 기술, 재료 또는 원리
CC0 퍼블릭 도메인
이 블루프린트는 CC0로 공개되었습니다. 어떤 목적으로든 자유롭게 복사, 수정, 배포 및 사용할 수 있습니다.
제품 구매를 통해 메이커를 지원하세요. 판매자가 설정한 메이커 커미션 을 받거나, 이 블루프린트의 새로운 반복을 만들어 연결로 포함시킬 수 있습니다.