Plug Gauge: Machinery Steel Case-Hardened in Charred Leather (Markham, 1908)
A plug gauge checks the size of a hole. Hardened tool steel can creep in size for months, so some makers used machinery steel and case-hardened it instead.
E. R. Markham's Tool Making (1908) packs the turned gauge in charred leather in a box, keeps it red hot in the furnace 7 or 8 hours, lets it cool, reheats it in a tube to a low red and plunges it in raw linseed oil. No tempering is needed, and the gauge does not change as it ages. Grinding and lapping are as for any plug gauge.
Mild steel stands for his machinery steel; the 3/4 in size is his Fig. 293.
Source: E. R. Markham, Tool Making (American School of Correspondence, 1908), pp. 178-182. Picture: his Fig. 295, ring laps in a holder.
උසස්
Two days
උපදෙස්
1
1
Read Markham
Read Markham
"When it reaches a low red heat, it should be plunged in a bath of raw linseed oil. It will not be necessary to draw the temper, and the danger of alteration as it ages is done away with."
2
2
Turn, knurl and stamp
Turn, knurl and stamp
Rough out the bar, allowing enough to turn off the decarbonised skin. Turn the handle (B in Fig. 293) to size and knurl it, and turn and finish the neck (C). Mill a flat spot in the middle of the handle and stamp on it the size of the gauge and the name or mark of the part it gauges (some shops stamp on C instead). Stamp before finishing any gauging surface, as driving stamps stretches the steel. Then turn the gauging end (A) .010 to .015 in over the finished size to allow for grinding.
මෙම පියවර සඳහා ද්‍රව්‍ය:
මෘදු වානේ දණ්ඩ1 barඅවශ්‍ය මෙවලම්:
ලෝහ කරකැවුම් යන්ත්‍රය
ලේත් කැපුම් මෙවලම
නර්ලිං මෙවලම
මිලින යන්ත්‍රය
වානේ අකුරු සහ ඉලක්කම් මුද්‍රා
මිටිය
මයික්‍රොමීටරය
ආරක්ෂිත කණ්ණාඩි3
3
Pack and carburise
Pack and carburise
Pack the gauge in a box with charred leather all round it, as for pack hardening, close the box and run it in the furnace for 7 or 8 hours. Then, red hot, take the box out of the furnace and let it cool with the gauge inside. Do not quench straight from the box: Markham's second heat refines the grain, making it as compact as properly hardened tool steel.
මෙම පියවර සඳහා ද්‍රව්‍ය:
අඟුරු කළ සම්1 packingඅවශ්‍ය මෙවලම්:
කේස් හාඩනිං පෙට්ටිය
මෆල් උදුනආරක්ෂිත කණ්ණාඩි4
4
Reheat and quench in oil
Reheat and quench in oil
Heat the gauge in an ordinary fire, enclosed in a piece of tube so the fire does not touch it. When it reaches a low red heat, plunge it into a bath of raw linseed oil. The temper need not be drawn.
අවශ්‍ය මෙවලම්:
කම්මල් උදුන
අමු හණ ඇට තෙල්ආරක්ෂිත කණ්ණාඩි5
5
Grind
Grind
Grind on dead centres if you can (a worn lathe spindle copies its own error onto the work), with water running on the work to keep it cool; otherwise heat it as little as possible. Use a coarse wheel free from glaze to within .004 in of size, then a finer wheel to .001 in over. Always measure the gauge cold, since a gauge ground to size while warm will be small when it cools.
අවශ්‍ය මෙවලම්:
සිලින්ඩරාකාර ඇඹරුම් යන්ත්රයමයික්රොමීටරයආරක්ෂිත කණ්ණාඩි6
6
Lap to size
Lap to size
Make a lap: a piece of cast iron with a hole bored a trifle larger than the gauge, split, and closed by a screw (Fig. 294); for much gauge work, a holder with split ring laps held by a pointed screw (Fig. 295). Lap the gauge to finished size with flour emery mixed with oil. Lapping warms it too much to caliper, so cool it in a dish of water at the temperature of the room where it will be used (about 70 F), not cold water, before each measurement.
අවශ්‍ය මෙවලම්:
වාත්තු යකඩ දණ්ඩ
එමරි කුඩු
යන්ත්‍ර තෙල්
වීදුරු බීකරය
ආසවනය කළ ජලය
රසායනාගාර උෂ්ණත්වමානයමයික්රොමීටරය7
7
History and honest limits
History and honest limits
Markham notes that the creeping of hardened tool steel, put down to a rearrangement of its particles after hardening, led some manufacturers to use machinery steel for gauges. The case-hardened gauge needs no seasoning.
He calls the steel "machinery steel"; mild steel bar stands for it here. The size of the box and the furnace are not given; the 3/4 in size is his Fig. 293.
ද්‍රව්‍ය
2- 1 barස්ථානගත
- 1 packingස්ථානගත
අවශ්‍ය මෙවලම්
19- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
මෙම සැලසුම සාදන්නේ
සම්බන්ධ බ්ලූප්‍රින්ට්
මෙම බ්ලූප්‍රින්ට් දැනුම බෙදා ගනී — ශිල්ප ක්‍රම, ද්‍රව්‍ය හෝ මූලධර්ම
CC0 පොදු වසම
මෙම බ්ලූප්‍රින්ට් CC0 යටතේ නිකුත් කර ඇත. ඔබට අවසර නොමැතිව පිටපත් කිරීම, වෙනස් කිරීම, බෙදා හැරීම සහ භාවිතා කිරීම කළ හැක.
බ්ලූප්‍රින්ට් හරහා නිෂ්පාදන මිලදී ගැනීමෙන් නිර්මාතෘට සහාය වන්න නිර්මාතෘ කොමිසම විකුණුම්කරුවන් විසින් නියම කළ, හෝ මෙම බ්ලූප්‍රින්ට්හි නව අනුවාදයක් සාදා ආදායම බෙදා ගැනීමට ඔබේ බ්ලූප්‍රින්ට්හි සම්බන්ධතාවයක් ලෙස ඇතුළත් කරන්න.