Metal Oxide Varistor: Zinc Oxide with 0.2 % Bismuth Oxide, 750 °C, 1.0 mm (Masuyama 1972)
A non-linear resistor: the current through it rises far faster than the voltage across it. Masuyama, Matsuoka and Nishi made one from zinc oxide with a little bismuth oxide: pressed into a disc, sintered, lapped, and given metal electrodes. With 0.2 mole % bismuth oxide, sintered at 750 °C and lapped to 1.0 mm, the disc measured a C-value of 200 at 1 mA and a nonlinearity exponent n of 1.8.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 1. Unknown: what the silver paint is. The patent calls the spraying and the paint well known. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
උසස්
1 day
උපදෙස්
1
1
Weigh 99.8 : 0.2 and wet-mill 5 hours
Weigh 99.8 : 0.2 and wet-mill 5 hours
Mix zinc oxide and bismuth oxide 99.8 : 0.2 by moles. Ours, for 10 g: 9.887 g zinc oxide, 0.113 g bismuth oxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
මෙම පියවර සඳහා ද්‍රව්‍ය:
සින්ක් ඔක්සයිඩ් කුඩු9.887 ග්‍රෑ
බිස්මත් ඔක්සයිඩ්0.113 ග්රෑඅවශ්ය මෙවලම්:
තුලාව
යකඩ බෝල් මිල
වේළන උදුන2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm².
අවශ්‍ය මෙවලම්:
හයිඩ්‍රොලික් මුද්‍රණ යන්ත්‍රය
තැටි තද කරන ඩයිය
වර්නියර් කැලිපරය3
3
Sinter 1 hour at 750 °C and furnace-cool
Sinter 1 hour at 750 °C and furnace-cool
Sinter the discs in air for 1 hour at 750 °C, then let them cool in the furnace to room temperature (about 15-30 °C). Masuyama gives 800 to 1200 °C as the best range for zinc oxide with bismuth oxide.
අවශ්‍ය මෙවලම්:
මෆල් උදුන4
4
Lap both faces to 1.0 mm
Lap both faces to 1.0 mm
Lap both faces with 600-mesh silicon carbide until the disc is 1.0 mm thick.
අවශ්‍ය මෙවලම්:
සිලිකන් කාබයිඩ් දැල්ලවර්නියර් කැලිපරය5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
මෙම පියවර සඳහා ද්‍රව්‍ය:
ඇලුමිනියම් කැටය1 as 3.2 mm spray wire
රිදී සන්නායක තීන්ත1 as required
තඹ කම්බිය2 කැබලිඅවශ්ය මෙවලම්:
වර්නියර් කැලිපරය
කම්බි-චාප ඉසින තුවක්කුව
කාර්මික වායු සම්පීඩකයද්රව්ය
5- 9.887 ග්රෑස්ථානගත
- 0.113 ග්රෑස්ථානගත
- 1 as 3.2 mm spray wireස්ථානගත
- 1 as requiredස්ථානගත
- 2 කැබලිස්ථානගත
අවශ්‍ය මෙවලම්
10- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
මෙම සැලසුම සාදන්නේ
සම්බන්ධ බ්ලූප්‍රින්ට්
මෙම බ්ලූප්‍රින්ට් දැනුම බෙදා ගනී — ශිල්ප ක්‍රම, ද්‍රව්‍ය හෝ මූලධර්ම
CC0 පොදු වසම
මෙම බ්ලූප්‍රින්ට් CC0 යටතේ නිකුත් කර ඇත. ඔබට අවසර නොමැතිව පිටපත් කිරීම, වෙනස් කිරීම, බෙදා හැරීම සහ භාවිතා කිරීම කළ හැක.
බ්ලූප්‍රින්ට් හරහා නිෂ්පාදන මිලදී ගැනීමෙන් නිර්මාතෘට සහාය වන්න නිර්මාතෘ කොමිසම විකුණුම්කරුවන් විසින් නියම කළ, හෝ මෙම බ්ලූප්‍රින්ට්හි නව අනුවාදයක් සාදා ආදායම බෙදා ගැනීමට ඔබේ බ්ලූප්‍රින්ට්හි සම්බන්ධතාවයක් ලෙස ඇතුළත් කරන්න.