Metal Oxide Varistor: Zinc Oxide with Manganese and Boric Oxides, Bismuth Paste Fired On (Masuyama 1972, Ex. 6)
A varistor with manganese dioxide and boric oxide mixed into the zinc oxide, and bismuth oxide fired on from a paste: 99.0 % zinc oxide, 0.5 % manganese dioxide and 0.5 % boric oxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 130 at 1 mA and a nonlinearity exponent n of 29.5.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 6. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
උසස්
2 days
උපදෙස්
1
1
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, manganese dioxide and boric oxide 99 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.904 g zinc oxide, 0.053 g manganese dioxide, 0.043 g boric oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
මෙම පියවර සඳහා ද්‍රව්‍ය:
සින්ක් ඔක්සයිඩ් කුඩු9.904 ග්‍රෑ
මැංගනීස් ඩයොක්සයිඩ් (පයිරොලුසයිට්)0.053 ග්‍රෑ
බෝරික් ඔක්සයිඩ්0.043 ග්රෑඅවශ්ය මෙවලම්:
තුලාව
යකඩ බෝල් මිල
වේළන උදුන2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
අවශ්‍ය මෙවලම්:
හයිඩ්‍රොලික් මුද්‍රණ යන්ත්‍රය
තැටි තද කරන ඩයිය
වර්නියර් කැලිපරය3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
අවශ්‍ය මෙවලම්:
මෆල් උදුන4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 6 gives no thickness.
අවශ්‍ය මෙවලම්:
සිලිකන් කාබයිඩ් දැල්ලවර්නියර් කැලිපරය5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
මෙම පියවර සඳහා ද්‍රව්‍ය:
බිස්මත් ඔක්සයිඩ්1 as requiredඅවශ්‍ය මෙවලම්:
එපොක්සි දුම්මල
n-බියුටනෝල්මෆල් උදුන6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
මෙම පියවර සඳහා ද්‍රව්‍ය:
ඇලුමිනියම් කැටය1 as 3.2 mm spray wire
රිදී සන්නායක තීන්ත1 as required
තඹ කම්බිය2 කැබලිඅවශ්ය මෙවලම්:
වර්නියර් කැලිපරය
කම්බි-චාප ඉසින තුවක්කුව
කාර්මික වායු සම්පීඩකයද්රව්ය
7- 9.904 ග්රෑස්ථානගත
- 0.053 ග්රෑස්ථානගත
- 0.043 ග්රෑස්ථානගත
- 1 as requiredස්ථානගත
- 1 as 3.2 mm spray wireස්ථානගත
- 1 as requiredස්ථානගත
- 2 කැබලිස්ථානගත
අවශ්‍ය මෙවලම්
12- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
- ස්ථානගත
මෙම සැලසුම සාදන්නේ
සම්බන්ධ බ්ලූප්‍රින්ට්
මෙම බ්ලූප්‍රින්ට් දැනුම බෙදා ගනී — ශිල්ප ක්‍රම, ද්‍රව්‍ය හෝ මූලධර්ම
CC0 පොදු වසම
මෙම බ්ලූප්‍රින්ට් CC0 යටතේ නිකුත් කර ඇත. ඔබට අවසර නොමැතිව පිටපත් කිරීම, වෙනස් කිරීම, බෙදා හැරීම සහ භාවිතා කිරීම කළ හැක.
බ්ලූප්‍රින්ට් හරහා නිෂ්පාදන මිලදී ගැනීමෙන් නිර්මාතෘට සහාය වන්න නිර්මාතෘ කොමිසම විකුණුම්කරුවන් විසින් නියම කළ, හෝ මෙම බ්ලූප්‍රින්ට්හි නව අනුවාදයක් සාදා ආදායම බෙදා ගැනීමට ඔබේ බ්ලූප්‍රින්ට්හි සම්බන්ධතාවයක් ලෙස ඇතුළත් කරන්න.