Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1250 °C, Presintered Twice at 900 °C (Snoek 1948, Ex. I)
A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, presintered twice at 900 °C, pressed into a ring and sintered at 1250 °C in oxygen. Snoek's ring had an initial permeability of 1,290.
Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. The violet iron oxide has its own blueprint (precipitated hematite calcined at 1000-1100 °C, after Nurdini et al. 2022); Snoek does not say how his was made. Picture: the patent's Fig. 4, the ring core.
Дээд шат
2 days
Зааварчилгаа
1
1
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Snoek does not say what makes it 'violet'; violet iron oxide has its own blueprint.
Энэ алхмын материал:
Зэсийн исэл13.24 г
Цайрын ислийн нунтаг20.32 г
Ягаан төмрийн исэл66.44 г
Манганы давхар исэл (пиролюзит)1 гШаардлагатай багаж:
Дэнсний жинлүүр
Тоосны маск2
2
Grind half an hour in an iron ball mill
Grind half an hour in an iron ball mill
Grind the mixture for half an hour in a mill with iron balls.
Шаардлагатай багаж:
Төмөр бөмбөлөгт тээрэмТоосны маск3
3
Presinter at 900 °C for 2 hours in oxygen
Presinter at 900 °C for 2 hours in oxygen
Heat the ground powder to 900 °C for 2 hours in oxygen and let it cool.
Шаардлагатай багаж:
Хоолойн зуух
Хүчилтөрөгч
Даралтат хийн баллон
Пирометр
Тагтай хайлуур (шаазан)
Халуунд тэсвэртэй бээлий4
4
Grind and presinter at 900 °C again (2 of 2)
Grind and presinter at 900 °C again (2 of 2)
Grind the powder, then heat it once more to 900 °C in oxygen. Snoek gives no times for the repeats.
Шаардлагатай багаж:
Төмөр бөмбөлөгт тээрэмХоолойн зуухХүчилтөрөгчДаралтат хийн баллонТагтай хайлуур (шаазан)Халуунд тэсвэртэй бээлийТоосны маск5
5
Grind 2 hours with iron balls
Grind 2 hours with iron balls
Grind it for 2 hours in a disintegrator with iron balls.
Шаардлагатай багаж:
Төмөр бөмбөлөгт тээрэмТоосны маск6
6
Press a ring at 4 tons per cm²
Press a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.
Шаардлагатай багаж:
Гидравлик пресс
Цагираг шахах хэвТоосны маск7
7
Sinter at 1250 °C in oxygen, cool 5–10 °C a minute
Sinter at 1250 °C in oxygen, cool 5–10 °C a minute
Sinter the ring at 1250 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 1,290, measured at room temperature at 2 kHz.
Шаардлагатай багаж:
Хоолойн зуухХүчилтөрөгчДаралтат хийн баллонПирометр
Тигелийн хямсааХалуунд тэсвэртэй бээлийМатериал
4- 13.24 гТүр орлуулагч
- 20.32 гТүр орлуулагч
- 66.44 гТүр орлуулагч
- Түр орлуулагч
Шаардлагатай багаж
12- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
Энэ загвараар хийдэг
Холбоотой загварууд
Эдгээр загварууд мэдлэг хуваалцдаг — арга техник, материал эсвэл зарчим
CC0 Нийтийн домэйн
Энэ загвар CC0 дор гаргагдсан. Та зөвшөөрөл авахгүйгээр хуулах, өөрчлөх, түгээх, ашиглах боломжтой.
Загвараар дамжуулан бүтээгдэхүүн худалдаж авч Бүтээгчийг дэмжээрэй Бүтээгчийн шимтгэл Борлуулагчаар тогтоосон, эсвэл энэ загварын шинэ хувилбар үүсгэж орлогоо хуваахын тулд өөрийн загварт холбоос болгон оруулна уу.