Barium Ferrite Disc Magnet: Example 4 Without the Orienting Field (Gorter, Philips 1956, Ex. 4 Comparison)
Made as in Example 4 but without the first, orienting field. Gorter's comparison block held 2,150 gauss with a coercive force of 2,000 oersted and a (BH)max of 0.9 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 4. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Дээд шат
3 days
Зааварчилгаа
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Энэ алхмын материал:
Барийн карбонат (витерит)450 г
Төмрийн (III) исэл2000 гШаардлагатай багаж:
Дэнсний жинлүүр
Резинэн бээлий
P100 амьсгалын хамгаалалт2
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
Шаардлагатай багаж:
Төмөр бөмбөлөгт тээрэм
Этанол - лабораторийн зэрэглэл, 95 %
Хатаах зуух3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
Шаардлагатай багаж:
Хоолойн зуух
Тагтай хайлуур (шаазан)
Халуунд тэсвэртэй бээлий4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
Шаардлагатай багаж:
Төмөр бөмбөлөгт тээрэмЭтанол - лабораторийн зэрэглэл, 95 %Хатаах зуух5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.
Шаардлагатай багаж:
Поливинил ацетат
АцетонДэнсний жинлүүр6
6
Mould without a first field
Mould without a first field
Put the suspension in a moulding die and remove the binder solution without any magnetic field. This is the patent's comparison block.
Шаардлагатай багаж:
Диск шахах хэв
Гидравлик пресс7
7
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
Шаардлагатай багаж:
Хоолойн зуух
ЭлектромагнитХалуунд тэсвэртэй бээлий8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
Шаардлагатай багаж:
Хоолойн зуухХалуунд тэсвэртэй бээлий9
9
Magnetise the block
Magnetise the block
Magnetise the block in a field. Without the orienting field it has no preferred direction. Ours: an electromagnet. Find the north face with a compass.
Шаардлагатай багаж:
Электромагнит
Луужин (компас)Материал
2- Түр орлуулагч
- 2000 гТүр орлуулагч
Шаардлагатай багаж
15- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
Энэ загвараар хийдэг
Холбоотой загварууд
Эдгээр загварууд мэдлэг хуваалцдаг — арга техник, материал эсвэл зарчим
CC0 Нийтийн домэйн
Энэ загвар CC0 дор гаргагдсан. Та зөвшөөрөл авахгүйгээр хуулах, өөрчлөх, түгээх, ашиглах боломжтой.
Загвараар дамжуулан бүтээгдэхүүн худалдаж авч Бүтээгчийг дэмжээрэй Бүтээгчийн шимтгэл Борлуулагчаар тогтоосон, эсвэл энэ загварын шинэ хувилбар үүсгэж орлогоо хуваахын тулд өөрийн загварт холбоос болгон оруулна уу.