Oriented Barium Ferrite Disc Magnet: Heated to 500 °C Without a Field (Gorter, Philips 1956, Ex. 6)
A ceramic magnet oriented in the die as in Example 4, but heated to 500 °C with no second field before sintering at 1280 °C. In the principal direction it held 3,025 gauss with a coercive force of 1,550 oersted and a (BH)max of 1.58 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 6. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Дээд шат
3 days
Зааварчилгаа
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Энэ алхмын материал:
Барийн карбонат (витерит)450 г
Төмрийн (III) исэл2000 гШаардлагатай багаж:
Дэнсний жинлүүр
Резинэн бээлий
P100 амьсгалын хамгаалалт2
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
Шаардлагатай багаж:
Төмөр бөмбөлөгт тээрэм
Этанол - лабораторийн зэрэглэл, 95 %
Хатаах зуух3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
Шаардлагатай багаж:
Хоолойн зуух
Тагтай хайлуур (шаазан)
Халуунд тэсвэртэй бээлий4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
Шаардлагатай багаж:
Төмөр бөмбөлөгт тээрэмЭтанол - лабораторийн зэрэглэл, 95 %Хатаах зуух5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.
Шаардлагатай багаж:
Поливинил ацетат
АцетонДэнсний жинлүүр6
6
Orient in a 10000 oersted field
Orient in a 10000 oersted field
Put the suspension in a moulding die between the poles of a magnet and apply a first field of 10000 oersted. Remove the binder solution while the field is on (as in Example 4).
Шаардлагатай багаж:
Диск шахах хэв
Электромагнит
Гидравлик пресс7
7
Heat to 500 °C without a field
Heat to 500 °C without a field
Heat the blocks to 500 °C with no magnetic field.
Шаардлагатай багаж:
Хоолойн зуухХалуунд тэсвэртэй бээлий8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
Шаардлагатай багаж:
Хоолойн зуухХалуунд тэсвэртэй бээлий9
9
Magnetise in the principal direction
Magnetise in the principal direction
Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.
Шаардлагатай багаж:
Электромагнит
Луужин (компас)Материал
2- Түр орлуулагч
- 2000 гТүр орлуулагч
Шаардлагатай багаж
15- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
Энэ загвараар хийдэг
Холбоотой загварууд
Эдгээр загварууд мэдлэг хуваалцдаг — арга техник, материал эсвэл зарчим
CC0 Нийтийн домэйн
Энэ загвар CC0 дор гаргагдсан. Та зөвшөөрөл авахгүйгээр хуулах, өөрчлөх, түгээх, ашиглах боломжтой.
Загвараар дамжуулан бүтээгдэхүүн худалдаж авч Бүтээгчийг дэмжээрэй Бүтээгчийн шимтгэл Борлуулагчаар тогтоосон, эсвэл энэ загварын шинэ хувилбар үүсгэж орлогоо хуваахын тулд өөрийн загварт холбоос болгон оруулна уу.