Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 1 % Antimony Trioxide, 1350 °C (Masuyama 1972, Ex. 2)
Masuyama, Matsuoka and Nishi found that adding a second oxide to zinc oxide and bismuth oxide changes the varistor a great deal. This is their Example 2 with antimony trioxide: 98.5 % zinc oxide, 0.5 % bismuth oxide and 1.0 % antimony trioxide by moles, sintered at 1350 °C. The disc measured a C-value of 75 at 1 mA and a nonlinearity exponent n of 15.3.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 2. Unknown: what the silver paint is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Дээд шат
1 day
Зааварчилгаа
1
1
Weigh 98.5 : 0.5 : 1 and wet-mill 5 hours
Weigh 98.5 : 0.5 : 1 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide and antimony trioxide 98.5 : 0.5 : 1 by moles. Ours, for 10 g: 9.386 g zinc oxide, 0.273 g bismuth oxide, 0.341 g antimony trioxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Энэ алхмын материал:
Цайрын ислийн нунтаг9.386 г
Висмутын исэл0.273 г
Сурьмын триоксид0.341 гШаардлагатай багаж:
Дэнсний жинлүүр
Төмөр бөмбөлөгт тээрэм
Хатаах зуух2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Шаардлагатай багаж:
Гидравлик пресс
Диск шахах хэв
Верньер штатахуун (штангенциркуль)3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air for 1 hour at 1350 °C, then let them cool in the furnace to room temperature (about 15-30 °C).
Шаардлагатай багаж:
Муфель зуух4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
Шаардлагатай багаж:
Цахиурын карбидын ширхэгВерньер штатахуун (штангенциркуль)5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Энэ алхмын материал:
Хөнгөн цагаан гулдмай1 as 3.2 mm spray wire
Мөнгөн дамжуулагч будаг1 as required
Зэс утас2 ширхэгШаардлагатай багаж:
Верньер штатахуун (штангенциркуль)
Утсан нумын шүршигч буу
Үйлдвэрийн агаарын шахуургаМатериал
6- 9.386 гТүр орлуулагч
- 0.273 гТүр орлуулагч
- 0.341 гТүр орлуулагч
- 1 as 3.2 mm spray wireТүр орлуулагч
- 1 as requiredТүр орлуулагч
- 2 ширхэгТүр орлуулагч
Шаардлагатай багаж
10- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
Энэ загвараар хийдэг
Холбоотой загварууд
Эдгээр загварууд мэдлэг хуваалцдаг — арга техник, материал эсвэл зарчим
CC0 Нийтийн домэйн
Энэ загвар CC0 дор гаргагдсан. Та зөвшөөрөл авахгүйгээр хуулах, өөрчлөх, түгээх, ашиглах боломжтой.
Загвараар дамжуулан бүтээгдэхүүн худалдаж авч Бүтээгчийг дэмжээрэй Бүтээгчийн шимтгэл Борлуулагчаар тогтоосон, эсвэл энэ загварын шинэ хувилбар үүсгэж орлогоо хуваахын тулд өөрийн загварт холбоос болгон оруулна уу.