Metal Oxide Varistor: Zinc Oxide with 0.5 % Boric Oxide, Bismuth-Manganese Oxide Paste Fired On (Masuyama 1972, Ex. 7)
A varistor whose bismuth oxide and manganese dioxide are both fired on from a paste: 99.5 % zinc oxide with 0.5 % boric oxide by moles, sintered at 1350 °C, coated with a 70 : 30 bismuth oxide and manganese dioxide paste and fired at 800 °C. The disc measured a C-value of 64 at 1 mA and a nonlinearity exponent n of 37.5.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 7. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Дээд шат
2 days
Зааварчилгаа
1
1
Weigh 99.5 : 0.5 and wet-mill 5 hours
Weigh 99.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide and boric oxide 99.5 : 0.5 by moles. Ours, for 10 g: 9.957 g zinc oxide, 0.043 g boric oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Энэ алхмын материал:
Цайрын ислийн нунтаг9.957 г
Борын исэл0.043 гШаардлагатай багаж:
Дэнсний жинлүүр
Төмөр бөмбөлөгт тээрэм
Хатаах зуух2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Шаардлагатай багаж:
Гидравлик пресс
Диск шахах хэв
Верньер штатахуун (штангенциркуль)3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Шаардлагатай багаж:
Муфель зуух4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 7 gives no thickness.
Шаардлагатай багаж:
Цахиурын карбидын ширхэгВерньер штатахуун (штангенциркуль)5
5
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat both lapped faces with a paste whose solids are 70 % bismuth oxide and 30 % manganese dioxide by weight, and fire it in air at 800 °C for 30 minutes. Example 7 does not name the paste's liquid; ours: the epoxy-resin butyl-alcohol solution of Example 4. Not given: how much paste.
Энэ алхмын материал:
Висмутын исэл1 as required
Манганы давхар исэл (пиролюзит)1 as requiredШаардлагатай багаж:
Эпокси давирхай
n-БутанолМуфель зуух6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Энэ алхмын материал:
Хөнгөн цагаан гулдмай1 as 3.2 mm spray wire
Мөнгөн дамжуулагч будаг1 as required
Зэс утас2 ширхэгШаардлагатай багаж:
Верньер штатахуун (штангенциркуль)
Утсан нумын шүршигч буу
Үйлдвэрийн агаарын шахуургаМатериал
7- 9.957 гТүр орлуулагч
- 0.043 гТүр орлуулагч
- 1 as requiredТүр орлуулагч
- 1 as requiredТүр орлуулагч
- 1 as 3.2 mm spray wireТүр орлуулагч
- 1 as requiredТүр орлуулагч
- 2 ширхэгТүр орлуулагч
Шаардлагатай багаж
12- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
- Түр орлуулагч
Энэ загвараар хийдэг
Холбоотой загварууд
Эдгээр загварууд мэдлэг хуваалцдаг — арга техник, материал эсвэл зарчим
CC0 Нийтийн домэйн
Энэ загвар CC0 дор гаргагдсан. Та зөвшөөрөл авахгүйгээр хуулах, өөрчлөх, түгээх, ашиглах боломжтой.
Загвараар дамжуулан бүтээгдэхүүн худалдаж авч Бүтээгчийг дэмжээрэй Бүтээгчийн шимтгэл Борлуулагчаар тогтоосон, эсвэл энэ загварын шинэ хувилбар үүсгэж орлогоо хуваахын тулд өөрийн загварт холбоос болгон оруулна уу.