Barium-Strontium Ferrite Disc Magnet: 0.5 mol BaCO3, 0.5 mol SrCO3, 1260 °C (Went, Philips 1956, Ex. 28)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Dicipta oleh

Charlie

28. Oktober 2026DE
2
0
0
0
0

Barium-Strontium Ferrite Disc Magnet: 0.5 mol BaCO3, 0.5 mol SrCO3, 1260 °C (Went, Philips 1956, Ex. 28)

A ceramic magnet with both barium and strontium: 0.5 mol barium carbonate and 0.5 mol strontium carbonate to 3 mol iron oxide, milled 15 hours, pressed and passed through a 1260 °C furnace in 20 minutes. Went's rod held 1,665 gauss with a coercive force of 3,235 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 28. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lanjutan
2 days

Arahan

1

Weigh the carbonates and iron oxide

Weigh 99.2 g barium carbonate (0.5 mol), 73.8 g strontium carbonate (0.5 mol), 483.3 g ferric oxide (3 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Bahan untuk langkah ini:

Barium karbonat (witherit)Barium karbonat (witherit)99.2 g
Strontium karbonatStrontium karbonat73.8 g
Ferik OksidaFerik Oksida483.3 g

Alatan diperlukan:

Neraca dua piringNeraca dua piring
Sarung tangan getahSarung tangan getah
Alat Pernafasan P100Alat Pernafasan P100
2

Mill with alcohol 15 hours, dry

Grind the mixture with alcohol in a ball mill for 15 hours, then dry it.

Alatan diperlukan:

Kilang Bebola BesiKilang Bebola Besi
Etanol mutu makmal, 95 %Etanol mutu makmal, 95 %
Ketuhar pengeringanKetuhar pengeringan
3

Press the powder

Example 28 moulds a rod without giving the pressure. Ours: press discs at 1.5 tonnes per cm², the pressure of the patent's other examples.

Alatan diperlukan:

Mesin tekan hidraulikMesin tekan hidraulik
Acuan tekan cakeraAcuan tekan cakera
4

Pass through a 1260 °C zone in 20 minutes

Sinter at 1260 °C by passing the pieces through a 10 cm hot zone at 5 mm per minute: 20 minutes in the heat.

Alatan diperlukan:

Relau TiubRelau Tiub
Sarung Tangan Tahan HabaSarung Tangan Tahan Haba
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Alatan diperlukan:

ElektromagnetElektromagnet
KompasKompas

Bahan

3

Alatan Diperlukan

12

Blueprint ini membuat

Thumbnail
Pemegang tempat

Magnet Cakera

Free

6
0
1

Blueprint berkaitan

Blueprint ini berkongsi pengetahuan — teknik, bahan atau prinsip

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

oleh CharlieDE

Industri

9
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

oleh CharlieDE

Industri

12
0
0
0
0
0

CC0 Domain Awam

Blueprint ini dikeluarkan di bawah CC0. Anda bebas menyalin, mengubah, mengedar, dan menggunakan karya ini untuk sebarang tujuan, tanpa meminta kebenaran.

Sokong Pembuat dengan membeli produk melalui Blueprint mereka di mana mereka memperoleh Komisen Pembuat ditetapkan oleh Penjual, atau cipta iterasi baru Blueprint ini dan sertakan ia sebagai sambungan dalam Blueprint anda sendiri untuk berkongsi hasil.

Perbincangan

(0)

Log masuk untuk menyertai perbincangan

Memuatkan komen...