Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this copper-zinc ferrite ring at a lower heat: technical copper oxide, zinc oxide and iron oxide with 1 % brownstone, fired at 1050 °C, then held 14 hours at 600 °C, all in oxygen. His ring had an initial permeability of 385.
The picture: our diagram.
Lanjutan
2 days
Arahan
1
1
Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone
Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone
Mix technical copper oxide, zinc oxide and iron oxide in the molecular ratio 20.7 : 31.6 : 47.7 (on the pure oxides) and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.91 g copper oxide, 21.73 g zinc oxide and 64.36 g ferric oxide per 100 g, plus 1 g brownstone.
Bahan untuk langkah ini:
Kuprum Oksida13.91 g
Serbuk Zink Oksida21.73 g
Ferik Oksida64.36 g
Mangan dioksida (pirolusit)1 gAlatan diperlukan:
Neraca dua piring
Topeng Habuk2
2
Grind for 3 hours in an iron ball mill
Grind for 3 hours in an iron ball mill
Grind the mixture for 3 hours in a mill with iron balls.
Alatan diperlukan:
Kilang Bebola BesiTopeng Habuk3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.
Alatan diperlukan:
Mesin tekan hidraulik
Acuan Penekan Gelang
Air Suling4
4
Fire 1 hour at 1050 °C, hold 14 hours at 600 °C
Fire 1 hour at 1050 °C, hold 14 hours at 600 °C
Sinter the ring in oxygen at 1050 °C for 1 hour, cool it slowly to 600 °C and hold it there for 14 hours, all in oxygen, then let it cool further. Snoek's core had an initial permeability of 385.
Alatan diperlukan:
Relau Tiub
Oksigen
Silinder gas bertekanan
Pirometer
Penyepit Mangkuk Pijar
Sarung Tangan Tahan HabaBahan
4- 13.91 gPemegang Tempat
- 21.73 gPemegang Tempat
- 64.36 gPemegang Tempat
- Pemegang Tempat
Alatan Diperlukan
12- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
Blueprint ini membuat
Blueprint berkaitan
Blueprint ini berkongsi pengetahuan — teknik, bahan atau prinsip
CC0 Domain Awam
Blueprint ini dikeluarkan di bawah CC0. Anda bebas menyalin, mengubah, mengedar, dan menggunakan karya ini untuk sebarang tujuan, tanpa meminta kebenaran.
Sokong Pembuat dengan membeli produk melalui Blueprint mereka di mana mereka memperoleh Komisen Pembuat ditetapkan oleh Penjual, atau cipta iterasi baru Blueprint ini dan sertakan ia sebagai sambungan dalam Blueprint anda sendiri untuk berkongsi hasil.