Ferrite Toroid Core: Magnesium-Zinc Ferrite Fired at 1400 °C in Oxygen (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this magnesium-zinc ferrite ring: magnesia, zinc oxide and iron oxide ground together, moulded with water into a ring and fired in oxygen at 1400 °C for 1 hour, then cooled slowly. His ring had an initial permeability of 525.
The picture: our diagram.
Lanjutan
2 days
Arahan
1
1
Mix 26.5 : 26.5 : 47 mol
Mix 26.5 : 26.5 : 47 mol
Mix pure magnesium oxide, zinc oxide and iron oxide in the molecular ratio 26.5 : 26.5 : 47. Ours, by weight: 9.95 g magnesium oxide, 20.10 g zinc oxide and 69.95 g ferric oxide per 100 g.
Bahan untuk langkah ini:
Magnesium oksida9.95 g
Serbuk Zink Oksida20.1 g
Ferik Oksida69.95 gAlatan diperlukan:
Neraca dua piring
Topeng Habuk2
2
Grind for 3 hours in an iron ball mill
Grind for 3 hours in an iron ball mill
Grind the mixture for 3 hours in a mill with iron balls.
Alatan diperlukan:
Kilang Bebola BesiTopeng Habuk3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.
Alatan diperlukan:
Mesin tekan hidraulik
Acuan Penekan Gelang
Air Suling4
4
Fire 1 hour at 1400 °C, cool at 3 °C a minute
Fire 1 hour at 1400 °C, cool at 3 °C a minute
Heat the ring in oxygen to 1400 °C for 1 hour (instead of 1300 °C), then cool it in oxygen at about 3 °C per minute. Snoek's ring had an initial permeability of 525.
Alatan diperlukan:
Relau Tiub
Oksigen
Silinder gas bertekanan
Pirometer
Penyepit Mangkuk Pijar
Sarung Tangan Tahan HabaBahan
3- 9.95 gPemegang Tempat
- 20.1 gPemegang Tempat
- 69.95 gPemegang Tempat
Alatan Diperlukan
12- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
Blueprint ini membuat
Blueprint berkaitan
Blueprint ini berkongsi pengetahuan — teknik, bahan atau prinsip
CC0 Domain Awam
Blueprint ini dikeluarkan di bawah CC0. Anda bebas menyalin, mengubah, mengedar, dan menggunakan karya ini untuk sebarang tujuan, tanpa meminta kebenaran.
Sokong Pembuat dengan membeli produk melalui Blueprint mereka di mana mereka memperoleh Komisen Pembuat ditetapkan oleh Penjual, atau cipta iterasi baru Blueprint ini dan sertakan ia sebagai sambungan dalam Blueprint anda sendiri untuk berkongsi hasil.