Strontium Ferrite Disc Magnet: Presintered, 4 Minutes at 1150 °C (Went, Philips 1956, Ex. 25)
A strontium ferrite with more strontium: 0.4 mol strontium carbonate to 0.8 mol iron oxide, milled, presintered at 1000 °C, milled again, pressed and passed through a 1150 °C furnace in 4 minutes. Went's rod held 1,200 gauss with a coercive force of 3,710 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 25. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lanjutan
2 days
Arahan
1
1
Dry the strontium carbonate and weigh
Dry the strontium carbonate and weigh
Dry the strontium carbonate at 100 °C. Weigh 59.05 g of it (0.4 mol) and 127.5 g ferric oxide (0.8 mol).
Bahan untuk langkah ini:
Strontium karbonat59.05 g
Ferik Oksida127.5 gAlatan diperlukan:
Ketuhar pengeringan
Neraca dua piring
Alat Pernafasan P1002
2
Mill 7 hours, dry at 110 °C
Mill 7 hours, dry at 110 °C
Grind with alcohol in a ball mill for 7 hours and dry at 110 °C.
Alatan diperlukan:
Kilang Bebola Besi
Etanol mutu makmal, 95 %Ketuhar pengeringan3
3
Presinter in air at 1000 °C for 4 hours
Presinter in air at 1000 °C for 4 hours
Fire in air at 1000 °C for 4 hours.
Alatan diperlukan:
Relau Muffle
Mangkuk pijar bertutup (porselin)
Penyepit Mangkuk Pijar
Sarung Tangan Tahan Haba4
4
Mill again, dry, press at 1.5 t/cm²
Mill again, dry, press at 1.5 t/cm²
Grind again 7 hours with alcohol, dry at 110 °C and press at 1.5 tonnes per cm² (ours: discs).
Alatan diperlukan:
Kilang Bebola BesiEtanol mutu makmal, 95 %Ketuhar pengeringan
Mesin tekan hidraulik
Acuan tekan cakera5
5
Pass through a 1150 °C zone in 4 minutes
Pass through a 1150 °C zone in 4 minutes
Sinter at 1150 °C by passing the pieces through a 4 cm hot zone at 10 mm per minute: 4 minutes in the heat.
Alatan diperlukan:
Relau TiubSarung Tangan Tahan Haba6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Alatan diperlukan:
Elektromagnet
KompasBahan
2- 59.05 gPemegang Tempat
- 127.5 gPemegang Tempat
Alatan Diperlukan
14- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
Blueprint ini membuat
Blueprint berkaitan
Blueprint ini berkongsi pengetahuan — teknik, bahan atau prinsip
CC0 Domain Awam
Blueprint ini dikeluarkan di bawah CC0. Anda bebas menyalin, mengubah, mengedar, dan menggunakan karya ini untuk sebarang tujuan, tanpa meminta kebenaran.
Sokong Pembuat dengan membeli produk melalui Blueprint mereka di mana mereka memperoleh Komisen Pembuat ditetapkan oleh Penjual, atau cipta iterasi baru Blueprint ini dan sertakan ia sebagai sambungan dalam Blueprint anda sendiri untuk berkongsi hasil.