Ytterbium: Oxide Reduced by Lanthanum at 1020 °C in Vacuum, Metal Distilled Off (Shindo and Yagi, US 2010/0260640)
Ytterbium boils far more easily than lanthanum. Heated with lanthanum in a vacuum, ytterbium oxide gives up its oxygen to the lanthanum, and the freed ytterbium leaves as vapour and condenses in a cooler zone, while lanthanum oxide stays behind.
Result: ytterbium metal ingots; 20 kg of distillate in the patent's run, low in sodium, potassium and lithium.
Source: Y. Shindo and K. Yagi, US patent application 2010/0260640 (2010), Example 1. Not given: how much lanthanum, the vacuum, the time, crucible and condenser materials. Picture drawn by Youblob.
Lanjutan
1 day
Arahan
1
1
Mix the oxide with lanthanum
Mix the oxide with lanthanum
Mix ytterbium oxide with lanthanum metal as the reducing agent. Not given: the proportions.
Bahan untuk langkah ini:
Iterbium oksida1 as requiredAlatan diperlukan:
Lantanum
Mangkuk pijar tantalum2
2
Reduce in vacuum at 1020 °C
Reduce in vacuum at 1020 °C
Heat the charge in a vacuum to 1020 °C: Yb2O3 + 2 La -> 2 Yb (vapour) + La2O3. Ours: a vacuum induction furnace; the vacuum level and time are not given.
Alatan diperlukan:
Relau aruhan
Pam vakumMangkuk pijar tantalum3
3
Condense the ytterbium at 200-600 °C
Condense the ytterbium at 200-600 °C
Catch the ytterbium vapour on a condenser held at 200-600 °C. Most of it settles in the 300-500 °C part; the 200-300 °C part carries the least sodium and lithium. Ours: a tantalum condenser plate.
Alatan diperlukan:
Plat pemeluwap tantalum4
4
Melt into ingots under argon
Melt into ingots under argon
Take the distillate off the condenser, melt it in a crucible at 950 °C under a slight pressure of argon, and let it solidify into an ingot.
Alatan diperlukan:
Mangkuk pijar tantalumRelau aruhan
ArgonBahan
1- 1 as requiredPemegang Tempat
Blueprint ini membuat
Blueprint berkaitan
Blueprint ini berkongsi pengetahuan — teknik, bahan atau prinsip
Berbahaya
Erbium, Ytterbium, Thulium and Lutetium Oxides: Xenotime Separated on Ion Exchange Columns with EDTA and HEDTA (Spedding and Powell, US 2,956,858)
oleh Charlie
Bukan Organik
6
0
0
0
0
0
Berbahaya
Lanthanum: Anhydrous Chloride Reduced with Calcium in a Tantalum Bomb under Argon, then Vacuum Cast (Daane, Ames 1950)
oleh Charlie
Bukan Organik
7
0
0
0
0
0
CC0 Domain Awam
Blueprint ini dikeluarkan di bawah CC0. Anda bebas menyalin, mengubah, mengedar, dan menggunakan karya ini untuk sebarang tujuan, tanpa meminta kebenaran.
Sokong Pembuat dengan membeli produk melalui Blueprint mereka di mana mereka memperoleh Komisen Pembuat ditetapkan oleh Penjual, atau cipta iterasi baru Blueprint ini dan sertakan ia sebagai sambungan dalam Blueprint anda sendiri untuk berkongsi hasil.