Metal Oxide Varistor: Zinc Oxide with Bismuth and Titanium Oxides, 1350 °C (Masuyama 1972)
Masuyama, Matsuoka and Nishi found that adding a second oxide to zinc oxide and bismuth oxide changes the varistor a great deal. This is their Example 2 with titanium dioxide: 99.0 % zinc oxide, 0.5 % bismuth oxide and 0.5 % titanium dioxide by moles, sintered at 1350 °C. The disc measured a C-value of 8.2 at 1 mA and a nonlinearity exponent n of 6.4.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 2. Unknown: what the silver paint is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Lanjutan
1 day
Arahan
1
1
Weigh 99.0 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99.0 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide and titanium dioxide 99.0 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.672 g zinc oxide, 0.28 g bismuth oxide, 0.048 g titanium dioxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Bahan untuk langkah ini:
Serbuk Zink Oksida9.672 g
Bismut oksida0.28 g
Titanium dioksida0.048 gAlatan diperlukan:
Neraca dua piring
Kilang Bebola Besi
Ketuhar pengeringan2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Alatan diperlukan:
Mesin tekan hidraulik
Acuan tekan cakera
Angkup Vernier3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air at 1350 °C for 1 hour, then let them cool in the furnace to room temperature (about 15-30 °C).
Alatan diperlukan:
Relau Muffle4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
Alatan diperlukan:
Grit silikon karbidaAngkup Vernier5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Bahan untuk langkah ini:
Jongkong aluminium1 as 3.2 mm spray wire
Cat perak konduktif1 as required
Dawai Tembaga2 kepingAlatan diperlukan:
Angkup Vernier
Pistol semburan arka wayar
Pemampat udara industriBahan
6- 9.672 gPemegang Tempat
- 0.28 gPemegang Tempat
- 0.048 gPemegang Tempat
- 1 as 3.2 mm spray wirePemegang Tempat
- 1 as requiredPemegang Tempat
- 2 kepingPemegang Tempat
Alatan Diperlukan
10- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
- Pemegang Tempat
Blueprint ini membuat
Blueprint berkaitan
Blueprint ini berkongsi pengetahuan — teknik, bahan atau prinsip
CC0 Domain Awam
Blueprint ini dikeluarkan di bawah CC0. Anda bebas menyalin, mengubah, mengedar, dan menggunakan karya ini untuk sebarang tujuan, tanpa meminta kebenaran.
Sokong Pembuat dengan membeli produk melalui Blueprint mereka di mana mereka memperoleh Komisen Pembuat ditetapkan oleh Penjual, atau cipta iterasi baru Blueprint ini dan sertakan ia sebagai sambungan dalam Blueprint anda sendiri untuk berkongsi hasil.