Ytterbium: Oxide Reduced by Lanthanum at 1020 °C in Vacuum, Metal Distilled Off (Shindo and Yagi, US 2010/0260640)
Ytterbium boils far more easily than lanthanum. Heated with lanthanum in a vacuum, ytterbium oxide gives up its oxygen to the lanthanum, and the freed ytterbium leaves as vapour and condenses in a cooler zone, while lanthanum oxide stays behind.
Result: ytterbium metal ingots; 20 kg of distillate in the patent's run, low in sodium, potassium and lithium.
Source: Y. Shindo and K. Yagi, US patent application 2010/0260640 (2010), Example 1. Not given: how much lanthanum, the vacuum, the time, crucible and condenser materials. Picture drawn by Youblob.
Ilọsíwájú
1 day
Ìlànà
1
1
Mix the oxide with lanthanum
Mix the oxide with lanthanum
Mix ytterbium oxide with lanthanum metal as the reducing agent. Not given: the proportions.
Àwọn ohun èlò fún ìgbésẹ̀ yìí:
Ọ̀sáídì ytterbium1 as requiredÀwọn irinṣẹ́ tí a nílò:
Lanthanum
Ìkòkò yíyọ́ tántálọ́mù2
2
Reduce in vacuum at 1020 °C
Reduce in vacuum at 1020 °C
Heat the charge in a vacuum to 1020 °C: Yb2O3 + 2 La -> 2 Yb (vapour) + La2O3. Ours: a vacuum induction furnace; the vacuum level and time are not given.
Àwọn irinṣẹ́ tí a nílò:
Ìléru induction
Ẹ̀rọ ìfàfẹ́fẹ́jádeÌkòkò yíyọ́ tántálọ́mù3
3
Condense the ytterbium at 200-600 °C
Condense the ytterbium at 200-600 °C
Catch the ytterbium vapour on a condenser held at 200-600 °C. Most of it settles in the 300-500 °C part; the 200-300 °C part carries the least sodium and lithium. Ours: a tantalum condenser plate.
Àwọn irinṣẹ́ tí a nílò:
Pẹpẹ ìṣàkójọ tántálọ́ọ̀mù4
4
Melt into ingots under argon
Melt into ingots under argon
Take the distillate off the condenser, melt it in a crucible at 950 °C under a slight pressure of argon, and let it solidify into an ingot.
Àwọn irinṣẹ́ tí a nílò:
Ìkòkò yíyọ́ tántálọ́mùÌléru induction
ArgonÀwọn ohun-èlò
1- 1 as requiredÀyè
Ìtọ́nisọ́nà yìí ń ṣe
Blueprint tó jọra
Àwọn blueprint wọ̀nyí pín ìmọ̀ — ọ̀nà, ohun-èlò tàbí ìlànà
Léwu
Erbium, Ytterbium, Thulium and Lutetium Oxides: Xenotime Separated on Ion Exchange Columns with EDTA and HEDTA (Spedding and Powell, US 2,956,858)
láti ọwọ́ Charlie
Inorganic
2
0
0
0
0
0
Léwu
Lanthanum: Anhydrous Chloride Reduced with Calcium in a Tantalum Bomb under Argon, then Vacuum Cast (Daane, Ames 1950)
láti ọwọ́ Charlie
Inorganic
1
0
0
0
0
0
CC0 Àgbègbè Gbogbogbò
Blueprint yìí ti jáde lábẹ́ CC0. O lè ṣe àdàkọ, yí padà, pín, àti lò láìsí ìyọ̀ǹda.
Ṣàtìlẹ́yìn Olùṣẹ́dá nípa rírà àwọn ọjà nipasẹ̀ Blueprint wọn Ẹ̀san Olùṣẹ́dá tí àwọn Olùtajà gbé kalẹ̀, tàbí ṣẹ̀dá àtúnṣe tuntun ti Blueprint yìí kí o sì fi sínú Blueprint rẹ gẹ́gẹ́ bí ìsopọ̀ láti pín owó-wíwọlé.