Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 12 % Manganese Dioxide, 1350 °C (Masuyama 1972, Ex. 2)
Masuyama, Matsuoka and Nishi found that adding a second oxide to zinc oxide and bismuth oxide changes the varistor a great deal. This is their Example 2 with manganese dioxide: 87.5 % zinc oxide, 0.5 % bismuth oxide and 12 % manganese dioxide by moles, sintered at 1350 °C. The disc measured a C-value of 200 at 1 mA and a nonlinearity exponent n of 2.1.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 2. Unknown: what the silver paint is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Abantado
1 day
Mga Tagubilin
1
1
Weigh 87.5 : 0.5 : 12 and wet-mill 5 hours
Weigh 87.5 : 0.5 : 12 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide and manganese dioxide 87.5 : 0.5 : 12 by moles. Ours, for 10 g: 8.48 g zinc oxide, 0.277 g bismuth oxide, 1.242 g manganese dioxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Mga materyales para sa hakbang na ito:
Pulbos ng Zinc Oxide8.48 g
Bismuth oxide0.277 g
Manganese dioxide (pirolusita)1.242 gMga kailangang kasangkapan:
Timbangang panimbang
Gilingang Bolang Bakal
Hurnong pantuyo2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Mga kailangang kasangkapan:
Haydroliko na pandiin
Hulmahan sa pagpindot ng disk
Kalipers na Vernier3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air for 1 hour at 1350 °C, then let them cool in the furnace to room temperature (about 15-30 °C).
Mga kailangang kasangkapan:
Muffle furnace4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
Mga kailangang kasangkapan:
Butil ng silicon carbideKalipers na Vernier5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Mga materyales para sa hakbang na ito:
Bareta ng aluminyo1 as 3.2 mm spray wire
Pinturang pilak na nagdadala ng kuryente1 as required
Kawad na Tanso2 pirasoMga kailangang kasangkapan:
Kalipers na Vernier
Baril na pang-spray na may arko ng kawad
Pang-industriyang panipil ng hanginMga Materyales
6- 8.48 gPlaceholder
- 0.277 gPlaceholder
- Placeholder
- 1 as 3.2 mm spray wirePlaceholder
- 1 as requiredPlaceholder
- 2 pirasoPlaceholder
Mga Kinakailangang Kasangkapan
10- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
Ang blueprint na ito ay gumagawa ng
Kaugnay na Blueprint
Ang mga blueprint na ito ay nagbabahagi ng kaalaman — mga teknik, materyales, o prinsipyo
CC0 Pampublikong Domain
Ang blueprint na ito ay inilabas sa ilalim ng CC0. Malaya kang kumopya, magbago, mamahagi, at gumamit nang walang pahintulot.
Suportahan ang Maker sa pamamagitan ng pagbili ng mga produkto sa kanilang Blueprint Komisyon ng Maker itinakda ng mga Vendor, o lumikha ng bagong bersyon ng Blueprint na ito at isama bilang koneksyon sa iyong Blueprint upang ibahagi ang kita.