Metal Oxide Varistor: Zinc Oxide with Manganese and Antimony Oxides, Bismuth Paste Fired On (Masuyama 1972, Ex. 6)
A varistor with manganese dioxide and antimony trioxide mixed into the zinc oxide, and bismuth oxide fired on from a paste: 99.0 % zinc oxide, 0.5 % manganese dioxide and 0.5 % antimony trioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 190 at 1 mA and a nonlinearity exponent n of 34.5.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 6. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Abantado
2 days
Mga Tagubilin
1
1
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, manganese dioxide and antimony trioxide 99 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.771 g zinc oxide, 0.053 g manganese dioxide, 0.177 g antimony trioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Mga materyales para sa hakbang na ito:
Pulbos ng Zinc Oxide9.771 g
Manganese dioxide (pirolusita)0.053 g
Antimony trioxide0.177 gMga kailangang kasangkapan:
Timbangang panimbang
Gilingang Bolang Bakal
Hurnong pantuyo2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Mga kailangang kasangkapan:
Haydroliko na pandiin
Hulmahan sa pagpindot ng disk
Kalipers na Vernier3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Mga kailangang kasangkapan:
Muffle furnace4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 6 gives no thickness.
Mga kailangang kasangkapan:
Butil ng silicon carbideKalipers na Vernier5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Mga materyales para sa hakbang na ito:
Bismuth oxide1 as requiredMga kailangang kasangkapan:
Dagtang epoksi
n-ButanolMuffle furnace6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Mga materyales para sa hakbang na ito:
Bareta ng aluminyo1 as 3.2 mm spray wire
Pinturang pilak na nagdadala ng kuryente1 as required
Kawad na Tanso2 pirasoMga kailangang kasangkapan:
Kalipers na Vernier
Baril na pang-spray na may arko ng kawad
Pang-industriyang panipil ng hanginMga Materyales
7- 9.771 gPlaceholder
- Placeholder
- 0.177 gPlaceholder
- 1 as requiredPlaceholder
- 1 as 3.2 mm spray wirePlaceholder
- 1 as requiredPlaceholder
- 2 pirasoPlaceholder
Mga Kinakailangang Kasangkapan
12- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
Ang blueprint na ito ay gumagawa ng
Kaugnay na Blueprint
Ang mga blueprint na ito ay nagbabahagi ng kaalaman — mga teknik, materyales, o prinsipyo
Metal Oxide Varistor: Zinc Oxide with 0.2 % Bismuth Oxide, Sintered Disc (Masuyama 1972)
ni Ed
Industriyal
3
0
0
0
0
0
Metal Oxide Varistor: Zinc Oxide with 0.2 % Manganese Dioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
ni Ed
Industriyal
3
0
0
0
0
0
Antimony Trioxide: Roasted Antimony Fused with More Metal (Thorpe 1912)
ni Charlie
Industriyal
10
0
0
0
0
0
CC0 Pampublikong Domain
Ang blueprint na ito ay inilabas sa ilalim ng CC0. Malaya kang kumopya, magbago, mamahagi, at gumamit nang walang pahintulot.
Suportahan ang Maker sa pamamagitan ng pagbili ng mga produkto sa kanilang Blueprint Komisyon ng Maker itinakda ng mga Vendor, o lumikha ng bagong bersyon ng Blueprint na ito at isama bilang koneksyon sa iyong Blueprint upang ibahagi ang kita.