Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1250 °C, Presintered Twice at 900 °C (Snoek 1948, Ex. I)
A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, presintered twice at 900 °C, pressed into a ring and sintered at 1250 °C in oxygen. Snoek's ring had an initial permeability of 1,290.
Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. The violet iron oxide has its own blueprint (precipitated hematite calcined at 1000-1100 °C, after Nurdini et al. 2022); Snoek does not say how his was made. Picture: the patent's Fig. 4, the ring core.
اعلیٰ
2 days
ہدایات
1
1
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Snoek does not say what makes it 'violet'; violet iron oxide has its own blueprint.
اس مرحلے کے لیے مواد:
کاپر آکسائیڈ13.24 گرام
زنک آکسائیڈ سفوف20.32 گرام
بنفشی آئرن آکسائیڈ66.44 گرام
مینگنیز ڈائی آکسائیڈ (پائرولوسائٹ)1 گرامدرکار اوزار:
پلڑوں والی ترازو
گرد کا ماسک2
2
Grind half an hour in an iron ball mill
Grind half an hour in an iron ball mill
Grind the mixture for half an hour in a mill with iron balls.
درکار اوزار:
لوہے کی بال ملگرد کا ماسک3
3
Presinter at 900 °C for 2 hours in oxygen
Presinter at 900 °C for 2 hours in oxygen
Heat the ground powder to 900 °C for 2 hours in oxygen and let it cool.
درکار اوزار:
نلکی بھٹی
آکسیجن
دباؤ والی گیس کا سلنڈر
پائرومیٹر
ڈھکن سمیت کروسیبل (چینی مٹی)
حرارت روک دستانے4
4
Grind and presinter at 900 °C again (2 of 2)
Grind and presinter at 900 °C again (2 of 2)
Grind the powder, then heat it once more to 900 °C in oxygen. Snoek gives no times for the repeats.
درکار اوزار:
لوہے کی بال ملنلکی بھٹیآکسیجندباؤ والی گیس کا سلنڈرڈھکن سمیت کروسیبل (چینی مٹی)حرارت روک دستانےگرد کا ماسک5
5
Grind 2 hours with iron balls
Grind 2 hours with iron balls
Grind it for 2 hours in a disintegrator with iron balls.
درکار اوزار:
لوہے کی بال ملگرد کا ماسک6
6
Press a ring at 4 tons per cm²
Press a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.
درکار اوزار:
ہائیڈرولک پریس
رنگ پریسنگ ڈائیگرد کا ماسک7
7
Sinter at 1250 °C in oxygen, cool 5–10 °C a minute
Sinter at 1250 °C in oxygen, cool 5–10 °C a minute
Sinter the ring at 1250 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 1,290, measured at room temperature at 2 kHz.
درکار اوزار:
نلکی بھٹیآکسیجندباؤ والی گیس کا سلنڈرپائرومیٹر
کٹھالی کی چمٹیحرارت روک دستانےمواد
4- 13.24 گرامپلیس ہولڈر
- 20.32 گرامپلیس ہولڈر
- 66.44 گرامپلیس ہولڈر
- پلیس ہولڈر
درکار اوزار
12- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
یہ بلوپرنٹ بناتا ہے
متعلقہ بلیو پرنٹ
یہ بلیو پرنٹ علم بانٹتے ہیں — تکنیک، مواد یا اصول
CC0 پبلک ڈومین
یہ بلیو پرنٹ CC0 کے تحت جاری کیا گیا ہے۔ آپ اجازت لیے بغیر اس کام کو نقل، ترمیم، تقسیم اور کسی بھی مقصد کے لیے استعمال کرنے کے لیے آزاد ہیں۔
میکر کی حمایت کریں ان کے بلیو پرنٹ کے ذریعے پروڈکٹس خرید کر جہاں وہ میکر کمیشن وینڈرز کی طرف سے مقرر، کماتے ہیں، یا اس بلیو پرنٹ کی نئی تکرار بنائیں اور آمدنی شیئر کرنے کے لیے اسے اپنے بلیو پرنٹ میں کنکشن کے طور پر شامل کریں۔