Hydroxyl-Ended Silicone Oil: D4 Opened with Potash, Then Water (Ceyzeriat 1964)
A trace of hot potash opens the ring of D4 and strings it into a long, thick chain. Water added a little at a time then cuts the chains back and leaves hydroxyl groups on their ends, which is what later lets the oil cure into rubber. This is Louis Ceyzeriat's oil A, the base of every sealant in his patent: 21,000 centistokes, 0.15 % hydroxyl.
Source: L. Ceyzeriat (Rhône-Poulenc), US 3,133,891 (1964), column 4. His neutraliser was the precipitated silica Hi-Sil X303; we use our precipitated silica in its place. The potash mix and the equipment are ours. Picture drawn by Youblob.
اعلیٰ
2 days
ہدایات
1
1
Make the 10 % potash
Make the 10 % potash
Dissolve 0.5 part of potassium hydroxide in 4.5 parts of water (our arithmetic for 5 parts of a 10 % solution). All parts are by weight.
اس مرحلے کے لیے مواد:
پوٹاشیم ہائیڈرو آکسائیڈ0.5 parts
پانی4.5 partsدرکار اوزار:
شیشے کا برتن
پلڑوں والی ترازو2
2
Heat D4 with the potash under nitrogen
Heat D4 with the potash under nitrogen
Heat 5000 parts of octamethylcyclotetrasiloxane (it melts at 17.5 °C) with the 5 parts of 10 % potash at 150 °C for 3½ hours under nitrogen. The oil thickens to 31,000 centistokes while hot.
اس مرحلے کے لیے مواد:
آکٹا میتھائل سائیکلو ٹیٹرا سائلوکسین (D4)5000 partsدرکار اوزار:
شیشے کا کشید فلاسک
گرم پلیٹ
حرارت پیما
ہلانے کا آلہ
نائٹروجن گیس سلنڈر3
3
Add water a little at a time
Add water a little at a time
Still hot, add 16.5 parts of water in small portions over 3 hours 40 minutes. The hot oil thins to 1730 centistokes.
اس مرحلے کے لیے مواد:
پانی16.5 partsدرکار اوزار:
شیشے کا کشید فلاسکگرم پلیٹحرارت پیماہلانے کا آلہ4
4
Cool, then neutralise with silica
Cool, then neutralise with silica
Let it cool for 15 hours. Then stir in 50 parts of precipitated silica to neutralise the potash. The liquid now measures 13,400 centistokes at 25 °C.
اس مرحلے کے لیے مواد:
رسوب شدہ سلیکا50 partsدرکار اوزار:
شیشے کا کشید فلاسکہلانے کا آلہ5
5
Strip the volatiles at 195–200 °C
Strip the volatiles at 195–200 °C
Heat it to about 195–200 °C in a current of nitrogen, with a water condenser on the outlet. 655 parts of liquid distil over; 4345 parts of oil A stay in the boiler, 21,000 centistokes at 25 °C with 0.15 % hydroxyl groups.
درکار اوزار:
شیشے کا کشید فلاسک
مکثف کی کنڈلیگرم پلیٹحرارت پیمانائٹروجن گیس سلنڈر
ڈھکن والا شیشے کا مرتبانمواد
4- 0.5 partsپلیس ہولڈر
- 21 partsپلیس ہولڈر
- پلیس ہولڈر
- 50 partsپلیس ہولڈر
یہ بلوپرنٹ بناتا ہے
متعلقہ بلیو پرنٹ
یہ بلیو پرنٹ علم بانٹتے ہیں — تکنیک، مواد یا اصول
CC0 پبلک ڈومین
یہ بلیو پرنٹ CC0 کے تحت جاری کیا گیا ہے۔ آپ اجازت لیے بغیر اس کام کو نقل، ترمیم، تقسیم اور کسی بھی مقصد کے لیے استعمال کرنے کے لیے آزاد ہیں۔
میکر کی حمایت کریں ان کے بلیو پرنٹ کے ذریعے پروڈکٹس خرید کر جہاں وہ میکر کمیشن وینڈرز کی طرف سے مقرر، کماتے ہیں، یا اس بلیو پرنٹ کی نئی تکرار بنائیں اور آمدنی شیئر کرنے کے لیے اسے اپنے بلیو پرنٹ میں کنکشن کے طور پر شامل کریں۔