Barium Ferrite Disc Magnet: Example 2 Without the Orienting Field (Gorter, Philips 1956, Ex. 2 Comparison)
A ceramic magnet from pre-fired barium ferrite powder suspended in polyvinyl acetate in acetone, made as in Example 2 but without the first, orienting field. Made without the first field, Gorter's comparison block reached a (BH)max of only 0.8 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 2. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
اعلیٰ
3 days
ہدایات
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
اس مرحلے کے لیے مواد:
بیریم کاربونیٹ (وِدھرائٹ)450 گرام
فیرک آکسائیڈ2000 گرامدرکار اوزار:
پلڑوں والی ترازو
ربڑ کے دستانے
P100 سانس محافظ2
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
درکار اوزار:
لوہے کی بال مل
ایتھینول - تجربہ گاہ درجہ، 95 %
سُکھانے کا تنور3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
درکار اوزار:
نلکی بھٹی
ڈھکن سمیت کروسیبل (چینی مٹی)
حرارت روک دستانے4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
درکار اوزار:
لوہے کی بال ملایتھینول - تجربہ گاہ درجہ، 95 %سُکھانے کا تنور5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 4 cc of solution per 3 g of powder. The binder burns off later.
درکار اوزار:
پولی وینائل ایسیٹیٹ
ایسیٹونپلڑوں والی ترازو6
6
Mould without a first field
Mould without a first field
Put the suspension in a moulding die and remove the binder solution without any magnetic field. This is the patent's comparison block.
درکار اوزار:
ڈسک دبانے کا سانچا
ہائیڈرولک پریس7
7
Compress into a block
Compress into a block
Compress the powder into a block. The pressure is not given.
درکار اوزار:
ہائیڈرولک پریسڈسک دبانے کا سانچا8
8
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
درکار اوزار:
نلکی بھٹی
برقی مقناطیسحرارت روک دستانے9
9
Sinter: through a 1300 °C zone in 5 minutes
Sinter: through a 1300 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1300 °C with a 10 cm hot zone: about 5 minutes in the heat.
درکار اوزار:
نلکی بھٹیحرارت روک دستانے10
10
Magnetise the block
Magnetise the block
Magnetise the block in a field. Without the orienting field it has no preferred direction. Ours: an electromagnet. Find the north face with a compass.
درکار اوزار:
برقی مقناطیس
قطب نمامواد
2- 450 گرامپلیس ہولڈر
- 2000 گرامپلیس ہولڈر
درکار اوزار
15- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
یہ بلوپرنٹ بناتا ہے
متعلقہ بلیو پرنٹ
یہ بلیو پرنٹ علم بانٹتے ہیں — تکنیک، مواد یا اصول
CC0 پبلک ڈومین
یہ بلیو پرنٹ CC0 کے تحت جاری کیا گیا ہے۔ آپ اجازت لیے بغیر اس کام کو نقل، ترمیم، تقسیم اور کسی بھی مقصد کے لیے استعمال کرنے کے لیے آزاد ہیں۔
میکر کی حمایت کریں ان کے بلیو پرنٹ کے ذریعے پروڈکٹس خرید کر جہاں وہ میکر کمیشن وینڈرز کی طرف سے مقرر، کماتے ہیں، یا اس بلیو پرنٹ کی نئی تکرار بنائیں اور آمدنی شیئر کرنے کے لیے اسے اپنے بلیو پرنٹ میں کنکشن کے طور پر شامل کریں۔