Oriented Barium Ferrite Disc Magnet: Water Instead of a Binder (Gorter, Philips 1956, Ex. 5)
A ceramic magnet from pre-fired barium ferrite powder stirred into water, oriented in a magnetic field in the die, moulded into blocks and fired as in Example 4. In the principal direction it held 2,870 gauss with a coercive force of 1,610 oersted and a (BH)max of 1.57 × 10⁶; at right angles 1,625 gauss.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 5. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
اعلیٰ
3 days
ہدایات
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
اس مرحلے کے لیے مواد:
بیریم کاربونیٹ (وِدھرائٹ)450 گرام
فیرک آکسائیڈ2000 گرامدرکار اوزار:
پلڑوں والی ترازو
ربڑ کے دستانے
P100 سانس محافظ2
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
درکار اوزار:
لوہے کی بال مل
ایتھینول - تجربہ گاہ درجہ، 95 %
سُکھانے کا تنور3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
درکار اوزار:
نلکی بھٹی
ڈھکن سمیت کروسیبل (چینی مٹی)
حرارت روک دستانے4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
درکار اوزار:
لوہے کی بال ملایتھینول - تجربہ گاہ درجہ، 95 %سُکھانے کا تنور5
5
Stir into water
Stir into water
Stir the pre-fired powder with water, 2 cc of water per gram of powder.
درکار اوزار:
کشید کیا ہوا پانی6
6
Orient in a first field and mould
Orient in a first field and mould
Put the suspension in a moulding die, apply a first magnetic field and mould it into blocks. The patent does not give this field's strength.
درکار اوزار:
ڈسک دبانے کا سانچا
برقی مقناطیس
ہائیڈرولک پریس7
7
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
درکار اوزار:
نلکی بھٹیبرقی مقناطیسحرارت روک دستانے8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
درکار اوزار:
نلکی بھٹیحرارت روک دستانے9
9
Magnetise in the principal direction
Magnetise in the principal direction
Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.
درکار اوزار:
برقی مقناطیس
قطب نمامواد
2- 450 گرامپلیس ہولڈر
- 2000 گرامپلیس ہولڈر
درکار اوزار
14- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
یہ بلوپرنٹ بناتا ہے
متعلقہ بلیو پرنٹ
یہ بلیو پرنٹ علم بانٹتے ہیں — تکنیک، مواد یا اصول
CC0 پبلک ڈومین
یہ بلیو پرنٹ CC0 کے تحت جاری کیا گیا ہے۔ آپ اجازت لیے بغیر اس کام کو نقل، ترمیم، تقسیم اور کسی بھی مقصد کے لیے استعمال کرنے کے لیے آزاد ہیں۔
میکر کی حمایت کریں ان کے بلیو پرنٹ کے ذریعے پروڈکٹس خرید کر جہاں وہ میکر کمیشن وینڈرز کی طرف سے مقرر، کماتے ہیں، یا اس بلیو پرنٹ کی نئی تکرار بنائیں اور آمدنی شیئر کرنے کے لیے اسے اپنے بلیو پرنٹ میں کنکشن کے طور پر شامل کریں۔