Semi-Cured Phenolic Sheet: Paper Dipped in Phenol Resin and Part-Cured at 120-130 °C (Lucas, Western Electric, US 1,470,990)
Paper soaked in phenol resin is dried, then cured only part of the way, so the resin is stiff but not yet hard. Lucas did this before the final hot press so the press would not squeeze the resin out of the fibres.
Result: a dry, partly cured phenolic sheet that a later coat of phenolic resin can still bond into.
Source: Lucas, US 1,470,990 (Western Electric, 1923). Stopping before his final hot press is ours. Not given: the solvent in his resin, paper grade, mercerising strengths. Picture drawn by Youblob.
درمیانہ
1 hour
ہدایات
1
1
Dip the paper in phenol resin
Dip the paper in phenol resin
Run the paper through a bath of phenol resin of specific gravity about 0.970: about 2 minutes for plain paper, 1 minute or less if mercerised first. Ours: Liquid Bakelite as the resin; Lucas does not say how it was thinned.
اس مرحلے کے لیے مواد:
کاغذ1 as required
مائع بیکیلائٹ (فینول-فارملڈیہائیڈ تکثیفی حاصل)1 as requiredدرکار اوزار:
پری پریگ امپریگنیٹنگ لائن
کثافت پیما2
2
Optional: mercerise the paper first
Optional: mercerise the paper first
For faster, fuller soaking, first pass the paper through caustic soda, squeeze, wash in water, neutralise in an acid, wash again and dry. Strengths and the acid: not given.
درکار اوزار:
کاسٹک سوڈا (سوڈیم ہائیڈرو آکسائیڈ)پری پریگ امپریگنیٹنگ لائن3
3
Dry at about 90 °C
Dry at about 90 °C
Dry the soaked paper in an oven at about 90 °C, just long enough to dry it.
درکار اوزار:
سُکھانے کا تنور4
4
Part-cure at 120-130 °C
Part-cure at 120-130 °C
Pass the dry paper through a curing oven at 120-130 °C for about 10 minutes (Lucas's description; his claim 4 says 125 °C for about 10 seconds). The resin sets as stiff as the fibres, but does not harden through.
درکار اوزار:
کیورنگ اوون5
5
Dip again for 10-15 seconds and dry
Dip again for 10-15 seconds and dry
Dip the part-cured paper in phenol resin again for 10-15 seconds, then dry at about 90 °C until it can be wound on a reel. Stop here: the sheet is semi-cured. Lucas's next step, stacking and hot pressing, cures it fully.
اس مرحلے کے لیے مواد:
مائع بیکیلائٹ (فینول-فارملڈیہائیڈ تکثیفی حاصل)1 as requiredدرکار اوزار:
پری پریگ امپریگنیٹنگ لائنسُکھانے کا تنورمواد
2- 1 as requiredپلیس ہولڈر
- 1 as requiredپلیس ہولڈر
درکار اوزار
5- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
یہ بلوپرنٹ بناتا ہے
متعلقہ بلیو پرنٹ
یہ بلیو پرنٹ علم بانٹتے ہیں — تکنیک، مواد یا اصول
CC0 پبلک ڈومین
یہ بلیو پرنٹ CC0 کے تحت جاری کیا گیا ہے۔ آپ اجازت لیے بغیر اس کام کو نقل، ترمیم، تقسیم اور کسی بھی مقصد کے لیے استعمال کرنے کے لیے آزاد ہیں۔
میکر کی حمایت کریں ان کے بلیو پرنٹ کے ذریعے پروڈکٹس خرید کر جہاں وہ میکر کمیشن وینڈرز کی طرف سے مقرر، کماتے ہیں، یا اس بلیو پرنٹ کی نئی تکرار بنائیں اور آمدنی شیئر کرنے کے لیے اسے اپنے بلیو پرنٹ میں کنکشن کے طور پر شامل کریں۔