Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 0.03 % Manganese Dioxide, 1350 °C (Masuyama 1972, Ex. 2)
Masuyama, Matsuoka and Nishi found that adding a second oxide to zinc oxide and bismuth oxide changes the varistor a great deal. This is their Example 2 with manganese dioxide: 99.47 % zinc oxide, 0.5 % bismuth oxide and 0.03 % manganese dioxide by moles, sintered at 1350 °C. The disc measured a C-value of 16 at 1 mA and a nonlinearity exponent n of 2.6.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 2. Unknown: what the silver paint is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
اعلیٰ
1 day
ہدایات
1
1
Weigh 99.47 : 0.5 : 0.03 and wet-mill 5 hours
Weigh 99.47 : 0.5 : 0.03 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide and manganese dioxide 99.47 : 0.5 : 0.03 by moles. Ours, for 10 g: 9.717 g zinc oxide, 0.28 g bismuth oxide, 0.003 g manganese dioxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
اس مرحلے کے لیے مواد:
زنک آکسائیڈ سفوف9.717 گرام
بسمتھ آکسائیڈ0.28 گرام
مینگنیز ڈائی آکسائیڈ (پائرولوسائٹ)0.003 گرامدرکار اوزار:
پلڑوں والی ترازو
لوہے کی بال مل
سُکھانے کا تنور2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
درکار اوزار:
ہائیڈرولک پریس
ڈسک دبانے کا سانچا
ورنیئر کیلیپر3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air for 1 hour at 1350 °C, then let them cool in the furnace to room temperature (about 15-30 °C).
درکار اوزار:
مفل بھٹی4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
درکار اوزار:
سیلیکون کاربائیڈ کے دانےورنیئر کیلیپر5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
اس مرحلے کے لیے مواد:
ایلومینیم کی سل1 as 3.2 mm spray wire
چاندی کا موصل رنگ1 as required
تانبے کا تار2 ٹکڑےدرکار اوزار:
ورنیئر کیلیپر
وائر آرک اسپرے گن
صنعتی ہوا کا دابکمواد
6- 9.717 گرامپلیس ہولڈر
- 0.28 گرامپلیس ہولڈر
- 0.003 گرامپلیس ہولڈر
- 1 as 3.2 mm spray wireپلیس ہولڈر
- 1 as requiredپلیس ہولڈر
- 2 ٹکڑےپلیس ہولڈر
درکار اوزار
10- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
یہ بلوپرنٹ بناتا ہے
متعلقہ بلیو پرنٹ
یہ بلیو پرنٹ علم بانٹتے ہیں — تکنیک، مواد یا اصول
CC0 پبلک ڈومین
یہ بلیو پرنٹ CC0 کے تحت جاری کیا گیا ہے۔ آپ اجازت لیے بغیر اس کام کو نقل، ترمیم، تقسیم اور کسی بھی مقصد کے لیے استعمال کرنے کے لیے آزاد ہیں۔
میکر کی حمایت کریں ان کے بلیو پرنٹ کے ذریعے پروڈکٹس خرید کر جہاں وہ میکر کمیشن وینڈرز کی طرف سے مقرر، کماتے ہیں، یا اس بلیو پرنٹ کی نئی تکرار بنائیں اور آمدنی شیئر کرنے کے لیے اسے اپنے بلیو پرنٹ میں کنکشن کے طور پر شامل کریں۔