Metal Oxide Varistor: Zinc Oxide with Manganese and Chromic Oxides, Bismuth Paste Fired On (Masuyama 1972, Ex. 6)
A varistor with manganese dioxide and chromic oxide mixed into the zinc oxide, and bismuth oxide fired on from a paste: 99.0 % zinc oxide, 0.5 % manganese dioxide and 0.5 % chromic oxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 282 at 1 mA and a nonlinearity exponent n of 25.6.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 6. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
اعلیٰ
2 days
ہدایات
1
1
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, manganese dioxide and chromic oxide 99 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.854 g zinc oxide, 0.053 g manganese dioxide, 0.093 g chromic oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
اس مرحلے کے لیے مواد:
زنک آکسائیڈ سفوف9.854 گرام
مینگنیز ڈائی آکسائیڈ (پائرولوسائٹ)0.053 گرام
کرومک آکسائیڈ0.093 گرامدرکار اوزار:
پلڑوں والی ترازو
لوہے کی بال مل
سُکھانے کا تنور2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
درکار اوزار:
ہائیڈرولک پریس
ڈسک دبانے کا سانچا
ورنیئر کیلیپر3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
درکار اوزار:
مفل بھٹی4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 6 gives no thickness.
درکار اوزار:
سیلیکون کاربائیڈ کے دانےورنیئر کیلیپر5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
اس مرحلے کے لیے مواد:
بسمتھ آکسائیڈ1 as requiredدرکار اوزار:
ایپاکسی رال
این-بیوٹانولمفل بھٹی6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
اس مرحلے کے لیے مواد:
ایلومینیم کی سل1 as 3.2 mm spray wire
چاندی کا موصل رنگ1 as required
تانبے کا تار2 ٹکڑےدرکار اوزار:
ورنیئر کیلیپر
وائر آرک اسپرے گن
صنعتی ہوا کا دابکمواد
7- 9.854 گرامپلیس ہولڈر
- 0.053 گرامپلیس ہولڈر
- 0.093 گرامپلیس ہولڈر
- 1 as requiredپلیس ہولڈر
- 1 as 3.2 mm spray wireپلیس ہولڈر
- 1 as requiredپلیس ہولڈر
- 2 ٹکڑےپلیس ہولڈر
درکار اوزار
12- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
- پلیس ہولڈر
یہ بلوپرنٹ بناتا ہے
متعلقہ بلیو پرنٹ
یہ بلیو پرنٹ علم بانٹتے ہیں — تکنیک، مواد یا اصول
CC0 پبلک ڈومین
یہ بلیو پرنٹ CC0 کے تحت جاری کیا گیا ہے۔ آپ اجازت لیے بغیر اس کام کو نقل، ترمیم، تقسیم اور کسی بھی مقصد کے لیے استعمال کرنے کے لیے آزاد ہیں۔
میکر کی حمایت کریں ان کے بلیو پرنٹ کے ذریعے پروڈکٹس خرید کر جہاں وہ میکر کمیشن وینڈرز کی طرف سے مقرر، کماتے ہیں، یا اس بلیو پرنٹ کی نئی تکرار بنائیں اور آمدنی شیئر کرنے کے لیے اسے اپنے بلیو پرنٹ میں کنکشن کے طور پر شامل کریں۔