Barium Ferrite Disc Magnet: 1 mol BaCO3 to 2.5 mol Iron Oxide, 1310 °C (Went, Philips 1956, Ex. 1)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Autor

Charlie

28. październik 2026DE
0
0
0
0
0

Barium Ferrite Disc Magnet: 1 mol BaCO3 to 2.5 mol Iron Oxide, 1310 °C (Went, Philips 1956, Ex. 1)

Went's first barium ferrite: 1 mol barium carbonate to 2.5 mol iron oxide, milled 13.5 hours, bound, formed and passed through a 1310 °C furnace in 20 minutes. His rod held 1,200 gauss with a coercive force of 1,940 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 1. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Zaawansowany
2 days

Instrukcje

1

Weigh barium carbonate and iron oxide

Weigh 201.1 g barium carbonate (1 mol) and 400.5 g ferric oxide (2.5 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Materiały do tego kroku:

Węglan baru (witheryt)Węglan baru (witheryt)201.1 g
Tlenek żelaza(III)Tlenek żelaza(III)400.5 g

Potrzebne narzędzia:

Waga szalkowaWaga szalkowa
Rękawice gumoweRękawice gumowe
Półmaska P100Półmaska P100
2

Mill with alcohol 13.5 hours, dry and sieve

Grind the mixture with alcohol in a ball mill for 13.5 hours, then dry it and sieve it.

Potrzebne narzędzia:

Żelazny młyn kulowyŻelazny młyn kulowy
Etanol - klasa laboratoryjna, 95 %Etanol - klasa laboratoryjna, 95 %
Piec do suszeniaPiec do suszenia
PrzesiewaczPrzesiewacz
3

Knead with a binder and form

Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.

Potrzebne narzędzia:

Polialkohol winylowy w proszkuPolialkohol winylowy w proszku
Prasa hydraulicznaPrasa hydrauliczna
Matryca do prasowania krążkówMatryca do prasowania krążków
Piec do suszeniaPiec do suszenia
4

Pass through a 1310 °C zone in 20 minutes

Sinter in air at 1310 °C by passing the pieces through a 10 cm hot zone at 5 mm per minute: 20 minutes in the heat.

Potrzebne narzędzia:

Piec rurowyPiec rurowy
Rękawice żaroodporneRękawice żaroodporne
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Potrzebne narzędzia:

ElektromagnesElektromagnes
KompasKompas

Materiały

2

Wymagane narzędzia

14

Według tego planu powstaje

Thumbnail
Zastępczy

Magnes krążkowy

Free

1
0
1

Powiązane blueprinty

Te blueprinty dzielą się wiedzą — technikami, materiałami lub zasadami

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

autor: CharlieDE

Przemysłowy

1
0
0
0
0
0

CC0 Domena publiczna

Ten plan jest udostępniany na licencji CC0. Możesz go swobodnie kopiować, modyfikować, rozpowszechniać i wykorzystywać do dowolnych celów, bez konieczności uzyskiwania zgody.

Wesprzyj Makera kupując produkty przez jego plan, za co zarabia Prowizja Makera ustalony przez sprzedawców, lub stwórz nową iterację tego planu i dołącz go jako połączenie w swoim własnym planie, aby dzielić się przychodami.

Dyskusja

(0)

Zaloguj się aby dołączyć do dyskusji

Ładowanie komentarzy...