Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.2 mol SrCO3 to 1.1 mol Iron Oxide (Went, Philips 1956, Ex. 7)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Autor

Charlie

28. październik 2026DE
0
0
0
0
0

Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.2 mol SrCO3 to 1.1 mol Iron Oxide (Went, Philips 1956, Ex. 7)

A strontium ferrite: 0.2 mol strontium carbonate to 1.1 mol iron oxide, dried, milled, presintered 3.5 hours at 1100 °C, bound, formed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 2,155 gauss with a coercive force of 2,500 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 7. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Zaawansowany
2 days

Instrukcje

1

Weigh strontium carbonate and iron oxide

Weigh 29.5 g strontium carbonate (0.2 mol) and 176.1 g ferric oxide (1.1 mol).

Materiały do tego kroku:

Węglan strontuWęglan strontu29.5 g
Tlenek żelaza(III)Tlenek żelaza(III)176.1 g

Potrzebne narzędzia:

Waga szalkowaWaga szalkowa
Półmaska P100Półmaska P100
2

Dry at 200 °C, mill with alcohol 4 hours

Dry the mixture at 200 °C, then grind it with alcohol in a ball mill for 4 hours and dry it.

Potrzebne narzędzia:

Piec do suszeniaPiec do suszenia
Żelazny młyn kulowyŻelazny młyn kulowy
Etanol - klasa laboratoryjna, 95 %Etanol - klasa laboratoryjna, 95 %
3

Presinter in air at 1100 °C for 3.5 hours

Fire the powder in air at 1100 °C for about 3.5 hours.

Potrzebne narzędzia:

Piec muflowyPiec muflowy
Tygiel z pokrywką (porcelanowy)Tygiel z pokrywką (porcelanowy)
Szczypce do tyglaSzczypce do tygla
Rękawice żaroodporneRękawice żaroodporne
4

Add a binder and form, dry overnight

Add a binder as in Example 1 (polyvinyl alcohol or nitrocellulose). The patent extrudes rods; ours: press discs at 1.5 tonnes per cm². Dry overnight.

Potrzebne narzędzia:

Polialkohol winylowy w proszkuPolialkohol winylowy w proszku
Prasa hydraulicznaPrasa hydrauliczna
Matryca do prasowania krążkówMatryca do prasowania krążków
Piec do suszeniaPiec do suszenia
5

Pass through a 1280 °C zone in 10 minutes

Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Potrzebne narzędzia:

Piec rurowyPiec rurowy
Rękawice żaroodporneRękawice żaroodporne
6

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Potrzebne narzędzia:

ElektromagnesElektromagnes
KompasKompas

Materiały

2

Wymagane narzędzia

15

Według tego planu powstaje

Thumbnail
Zastępczy

Magnes krążkowy

Free

1
0
1

Powiązane blueprinty

Te blueprinty dzielą się wiedzą — technikami, materiałami lub zasadami

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

autor: CharlieDE

Przemysłowy

1
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

autor: CharlieDE

Przemysłowy

2
0
0
0
0
0

CC0 Domena publiczna

Ten plan jest udostępniany na licencji CC0. Możesz go swobodnie kopiować, modyfikować, rozpowszechniać i wykorzystywać do dowolnych celów, bez konieczności uzyskiwania zgody.

Wesprzyj Makera kupując produkty przez jego plan, za co zarabia Prowizja Makera ustalony przez sprzedawców, lub stwórz nową iterację tego planu i dołącz go jako połączenie w swoim własnym planie, aby dzielić się przychodami.

Dyskusja

(0)

Zaloguj się aby dołączyć do dyskusji

Ładowanie komentarzy...