Metal Oxide Varistor: Zinc Oxide with Bismuth, Manganese and Antimony Oxides, 1350 °C (Masuyama 1972, Ex. 3)
Masuyama, Matsuoka and Nishi found that adding two more oxides to zinc oxide and bismuth oxide gives excellent non-linear properties. This is their Example 3 with manganese dioxide and antimony trioxide: 98.5 % zinc oxide and 0.5 % each of bismuth oxide, manganese dioxide and antimony trioxide by moles, sintered at 1350 °C. The disc measured a C-value of 150 at 1 mA and a nonlinearity exponent n of 27.4.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 3. Unknown: how the aluminium is sprayed on and what the silver paint is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Zaawansowany
1 day
Instrukcje
1
1
Weigh 98.5 : 0.5 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 98.5 : 0.5 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide, manganese dioxide and antimony trioxide 98.5 : 0.5 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.5 g zinc oxide, 0.276 g bismuth oxide, 0.052 g manganese dioxide, 0.173 g antimony trioxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Materiały do tego kroku:
Proszek tlenku cynku9.5 g
Tlenek bizmutu0.276 g
Ditlenek manganu (piroluzyt)0.052 g
Tritlenek antymonu0.173 gPotrzebne narzędzia:
Waga szalkowa
Żelazny młyn kulowy
Piec do suszenia2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Potrzebne narzędzia:
Prasa hydrauliczna
Matryca do prasowania krążków
Suwmiarka3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air for 1 hour at 1350 °C, then let them cool in the furnace to room temperature (about 15-30 °C).
Potrzebne narzędzia:
Piec muflowy4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
Potrzebne narzędzia:
Ścierniwo z węglika krzemuSuwmiarka5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Unknown: the spraying method and the paint.
Materiały do tego kroku:
Wlewek aluminiowy1 as required
Srebrna farba przewodząca1 as required
Drut miedziany2 sztukPotrzebne narzędzia:
Nieznana metoda natryskiwania metaluSuwmiarkaMateriały
7- 9.5 gZastępnik
- 0.276 gZastępnik
- 0.052 gZastępnik
- 0.173 gZastępnik
- 1 as requiredZastępnik
- 1 as requiredZastępnik
- 2 sztukZastępnik
Wymagane narzędzia
9- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
Według tego planu powstaje
Powiązane blueprinty
Te blueprinty dzielą się wiedzą — technikami, materiałami lub zasadami
CC0 Domena publiczna
Ten plan jest udostępniany na licencji CC0. Możesz go swobodnie kopiować, modyfikować, rozpowszechniać i wykorzystywać do dowolnych celów, bez konieczności uzyskiwania zgody.
Wesprzyj Makera kupując produkty przez jego plan, za co zarabia Prowizja Makera ustalony przez sprzedawców, lub stwórz nową iterację tego planu i dołącz go jako połączenie w swoim własnym planie, aby dzielić się przychodami.