Metal Oxide Varistor: Pure Zinc Oxide at 1350 °C, Bismuth Oxide Paste Fired at 800 °C (Masuyama 1972, Ex. 4)
A varistor made the other way round: a disc of pure zinc oxide, sintered, with bismuth oxide fired into its faces from a paste instead of mixed in. Sintered at 1350 °C and fired with the paste at 800 °C, the disc measured a C-value of 90 at 1 mA and a nonlinearity exponent n of 7.3. Masuyama found that firing on the bismuth oxide paste raises n a great deal over mixing it in.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 4. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Zaawansowany
2 days
Instrukcje
1
1
Press pure zinc oxide at 340 kg/cm²
Press pure zinc oxide at 340 kg/cm²
Press zinc oxide powder at 340 kg/cm². Example 4 gives no disc size; ours: discs 13 mm across and 2.5 mm thick in the mould of Example 1.
Materiały do tego kroku:
Proszek tlenku cynku1 as requiredPotrzebne narzędzia:
Waga szalkowa
Prasa hydrauliczna
Matryca do prasowania krążków
Suwmiarka2
2
Sinter 1 hour at 1350 °C and cool
Sinter 1 hour at 1350 °C and cool
Heat the pressed disc for 1 hour at 1350 °C, then let it cool to room temperature.
Potrzebne narzędzia:
Piec muflowy3
3
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 4 gives no thickness.
Potrzebne narzędzia:
Ścierniwo z węglika krzemuSuwmiarka4
4
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Materiały do tego kroku:
Tlenek bizmutu1 as requiredPotrzebne narzędzia:
Żywica epoksydowa
n-ButanolPiec muflowy5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Materiały do tego kroku:
Wlewek aluminiowy1 as required
Srebrna farba przewodząca1 as required
Drut miedziany2 sztukPotrzebne narzędzia:
Nieznana metoda natryskiwania metaluSuwmiarkaMateriały
5- 1 as requiredZastępnik
- 1 as requiredZastępnik
- 1 as requiredZastępnik
- 1 as requiredZastępnik
- 2 sztukZastępnik
Wymagane narzędzia
9- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
Według tego planu powstaje
Powiązane blueprinty
Te blueprinty dzielą się wiedzą — technikami, materiałami lub zasadami
CC0 Domena publiczna
Ten plan jest udostępniany na licencji CC0. Możesz go swobodnie kopiować, modyfikować, rozpowszechniać i wykorzystywać do dowolnych celów, bez konieczności uzyskiwania zgody.
Wesprzyj Makera kupując produkty przez jego plan, za co zarabia Prowizja Makera ustalony przez sprzedawców, lub stwórz nową iterację tego planu i dołącz go jako połączenie w swoim własnym planie, aby dzielić się przychodami.