Metal Oxide Varistor: Zinc Oxide with Manganese and Titanium Oxides, Bismuth Paste Fired On (Masuyama 1972, Ex. 6)
A varistor with manganese dioxide and titanium dioxide mixed into the zinc oxide, and bismuth oxide fired on from a paste: 99.0 % zinc oxide, 0.5 % manganese dioxide and 0.5 % titanium dioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 66 at 1 mA and a nonlinearity exponent n of 13.7.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 6. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Zaawansowany
2 days
Instrukcje
1
1
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, manganese dioxide and titanium dioxide 99 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.898 g zinc oxide, 0.053 g manganese dioxide, 0.049 g titanium dioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Materiały do tego kroku:
Proszek tlenku cynku9.898 g
Ditlenek manganu (piroluzyt)0.053 g
Dwutlenek tytanu0.049 gPotrzebne narzędzia:
Waga szalkowa
Żelazny młyn kulowy
Piec do suszenia2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Potrzebne narzędzia:
Prasa hydrauliczna
Matryca do prasowania krążków
Suwmiarka3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Potrzebne narzędzia:
Piec muflowy4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 6 gives no thickness.
Potrzebne narzędzia:
Ścierniwo z węglika krzemuSuwmiarka5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Materiały do tego kroku:
Tlenek bizmutu1 as requiredPotrzebne narzędzia:
Żywica epoksydowa
n-ButanolPiec muflowy6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Materiały do tego kroku:
Wlewek aluminiowy1 as required
Srebrna farba przewodząca1 as required
Drut miedziany2 sztukPotrzebne narzędzia:
Nieznana metoda natryskiwania metaluSuwmiarkaMateriały
7- 9.898 gZastępnik
- 0.053 gZastępnik
- 0.049 gZastępnik
- 1 as requiredZastępnik
- 1 as requiredZastępnik
- 1 as requiredZastępnik
- 2 sztukZastępnik
Wymagane narzędzia
11- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
- Zastępnik
Według tego planu powstaje
Powiązane blueprinty
Te blueprinty dzielą się wiedzą — technikami, materiałami lub zasadami
CC0 Domena publiczna
Ten plan jest udostępniany na licencji CC0. Możesz go swobodnie kopiować, modyfikować, rozpowszechniać i wykorzystywać do dowolnych celów, bez konieczności uzyskiwania zgody.
Wesprzyj Makera kupując produkty przez jego plan, za co zarabia Prowizja Makera ustalony przez sprzedawców, lub stwórz nową iterację tego planu i dołącz go jako połączenie w swoim własnym planie, aby dzielić się przychodami.