Barium-Calcium Ferrite Disc Magnet: 5 % Calcium, Sintered at 1330 °C (Went, Philips 1956, Ex. 18)
A ceramic magnet with a twentieth of the barium replaced by calcium: 0.095 mol barium carbonate, 0.005 mol calcium carbonate and 0.6 mol iron oxide. It is milled, fired in air, milled again, pressed and passed through a 1330 °C furnace in 10 minutes. The X-ray picture showed only the magnetoplumbite phase. Went's rod held 1,680 gauss with a coercive force of 1,110 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 18. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Продвинутый
2 days
Инструкции
1
1
Weigh barium carbonate, chalk and iron oxide
Weigh barium carbonate, chalk and iron oxide
Weigh 18.74 g barium carbonate (0.095 mol), 0.5 g calcium carbonate (0.005 mol) and 95.55 g ferric oxide (0.6 mol). The patent used analytical-grade carbonates. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Материалы для этого шага:
Карбонат бария (витерит)18.74 г
Карбонат кальция (мел молотый)0.5 г
Оксид железа(III)95.55 гНеобходимые инструменты:
Рычажные весы
Резиновые перчатки
Респиратор P1002
2
Mill 4 hours, dry at 150 °C
Mill 4 hours, dry at 150 °C
Grind with alcohol in a ball mill for 4 hours and dry in air at 150 °C.
Необходимые инструменты:
Железная шаровая мельница
Этанол - лабораторной чистоты, 95 %
Сушильная печь3
3
Presinter in air at 1000 °C for 2 hours
Presinter in air at 1000 °C for 2 hours
Fire the dry powder in air at 1000 °C for 2 hours.
Необходимые инструменты:
Муфельная печь
Тигель с крышкой (фарфоровый)
Щипцы для тигля
Термостойкие перчатки4
4
Mill again, dry, press at 1.5 t/cm²
Mill again, dry, press at 1.5 t/cm²
Grind again with alcohol for 4 hours, dry, and press at 1.5 tonnes per cm² (ours: discs instead of rods).
Необходимые инструменты:
Железная шаровая мельницаЭтанол - лабораторной чистоты, 95 %Сушильная печь
Гидравлический пресс
Пресс-форма для дисков5
5
Pass through a 1330 °C zone in 10 minutes
Pass through a 1330 °C zone in 10 minutes
Sinter at 1330 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Необходимые инструменты:
Трубчатая печьТермостойкие перчатки6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Необходимые инструменты:
Электромагнит
КомпасМатериалы
3- 18.74 гЗаполнитель
- Заполнитель
- 95.55 гЗаполнитель
Требуемые инструменты
15- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
По этому чертежу делают
Связанные чертежи
Эти чертежи делятся знаниями — техники, материалы или принципы
CC0 Общественное достояние
Этот чертёж выпущен под лицензией CC0. Вы можете свободно копировать, изменять, распространять и использовать эту работу в любых целях без запроса разрешения.
Поддержите мейкера, покупая товары через его чертёж, где он получает Комиссию мейкера установленную продавцами, или создайте новую итерацию этого чертежа и включите его как связь в свой чертёж для распределения дохода.