High-Speed Steel, Charge 2: Crucible-Melted Tungsten-Chrome-Vanadium Steel (Carnegie & Gladwyn 1918)
High-speed steel holds its edge when it is cutting hot. In Sheffield it was made like other crucible tool steel: the best Swedish bar iron melted in small clay pots in a coke fire, with tungsten, vanadium and chromium added to the liquid iron. This is the second of three typical charges given by Carnegie and Gladwyn: 75 lb iron, 18.5 lb tungsten powder, 1 lb ferro-vanadium and 8 lb ferro-chrome for 100 lb of steel.
Source: D. Carnegie and S. C. Gladwyn, Liquid Steel (1918), pp. 74-77, 106-107 and 113. Unknown: how the Swedish iron, the tungsten powder and the ferro-vanadium are made; the melting time; and how the ingot is worked into bar. The book stops at the liquid steel, so these are linked to unknown heads. Picture: the book's Fig. 29, crucible furnaces at Samuel Osborn & Co., Sheffield.
Эксперт
1 day
Инструкции
1
1
Weigh charge 2
Weigh charge 2
For 100 lb of steel: 75 lb best Swedish bar iron, cut up; 18.5 lb tungsten powder (96 to 98 % tungsten); 1.0 lb ferro-vanadium (35 to 40 % vanadium); 8.0 lb ferro-chrome (60 % chromium). Unknown: how the Swedish iron, tungsten powder and ferro-vanadium are made. The book only lists them.
Материалы для этого шага:
Шведское полосовое железо75 фунты
Вольфрамовый порошок18.5 фунты
Феррованадий1 фунты
Феррохром8 фунтыНеобходимые инструменты:
Рычажные весы2
2
Set two clay crucibles in the melting hole
Set two clay crucibles in the melting hole
Tool steels are melted in small crucibles, about 55 lb each, two to a hole in a Huntsman coke furnace (ours: the 100 lb charge split between the two). Stand them on fireclay stands on the fire bars, straight from the annealing furnace, and fill the hole with coke up to their tops. Use the best washed coke, as free from sulphur as possible: sulphur gets into the steel even through the lid. When the pots are white hot, throw in a little sand to fuse them onto their stands.
Необходимые инструменты:
Тигельная печь
Тигель из огнеупорной глины
Металлургический кокс
Песок
Щипцы для тигля3
3
Melt the iron, then add the alloys
Melt the iron, then add the alloys
Charge the cut iron, put on the clay lids, fill the hole with coke and close the cover. Renew the fire as it burns through. Add the tungsten powder and ferro-alloys to the liquid iron and melt them in. Unknown: the melting time and temperature for this charge. The book says only that tool steel takes longer than ordinary steel. About 3½ tons of coke go to each ton of high-speed steel.
Необходимые инструменты:
Тигельная печьМеталлургический коксЩипцы для тигля4
4
Pull out, skim and teem
Pull out, skim and teem
Lift each pot out with the pulling-out tongs (arms and legs covered with wet sacking), take off the lid and skim the slag with a mop, then pour the steel into ingot moulds. Unknown: the ingot size. A clay crucible lasts about 3 heats.
Необходимые инструменты:
Щипцы для тигля
Изложница
Термостойкие перчатки5
5
Work the ingot into round bar
Work the ingot into round bar
Unknown: how the ingot is heated, hammered or rolled, and annealed into round bar. Carnegie and Gladwyn stop at the liquid steel, so this step is linked to an unknown head until a source gives it.
Необходимые инструменты:
Неизвестный режим ковкиМатериалы
4- 75 фунтыЗаполнитель
- 18.5 фунтыЗаполнитель
- 1 фунтыЗаполнитель
- 8 фунтыЗаполнитель
Требуемые инструменты
9- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
По этому чертежу делают
Связанные чертежи
Эти чертежи делятся знаниями — техники, материалы или принципы
Crucible Cast Steel by the Huntsman Process — Remelting Blister Steel into Flawless Ingots
от Tarkin
Металлообработка
58
0
0
0
0
0
Опасно
Ductile Tungsten Wire: Pressed, Sintered by Current, Swaged and Drawn Hot (Coolidge 1913)
от Forge
Металлообработка
11
0
0
0
0
0
High-Speed Steel, Charge 1: Crucible-Melted Tungsten-Chrome-Molybdenum Steel (Carnegie & Gladwyn 1918)
от Forge
Металлообработка
9
0
0
0
0
0
CC0 Общественное достояние
Этот чертёж выпущен под лицензией CC0. Вы можете свободно копировать, изменять, распространять и использовать эту работу в любых целях без запроса разрешения.
Поддержите мейкера, покупая товары через его чертёж, где он получает Комиссию мейкера установленную продавцами, или создайте новую итерацию этого чертежа и включите его как связь в свой чертёж для распределения дохода.