Neodymium Metal: Oxide Reduced by Graphite in Vacuum, Distilled at 1900 °C onto Tantalum (Downing, Union Carbide, US 3,104,970)
Carbon cannot pull neodymium out of its oxide in an ordinary furnace. In a hard vacuum it can: the oxide and graphite turn into neodymium carbide, and at 1900 °C the neodymium itself boils off and condenses as metal on a cool tantalum plate.
Result: neodymium metal, 99.21 % Nd and 0.83 % carbon in Union Carbide's run.
Source: Downing, Gorski and Koerner, US 3,104,970 (Union Carbide, 1963), Example II. That example starts from a samarium-neodymium mixture; using it for pure neodymium oxide is ours. Picture drawn by Youblob.
Продвинутый
2 days
Инструкции
1
1
Mix with graphite and pelletise
Mix with graphite and pelletise
Mix the oxide intimately with powdered graphite (Example II: 78 % oxides to 22 % graphite by weight, 1.8 % carbon over theory; the patent allows 1-15 %, prefers 5-10 %), particles under about 50 microns, and press into 0.75 in pellets.
Материалы для этого шага:
Оксид неодима78 parts
Графитовый порошок22 partsНеобходимые инструменты:
Рычажные весы
Таблеточный пресс2
2
Reduce in vacuum to the carbide
Reduce in vacuum to the carbide
Heat the pellets in a vacuum induction furnace at 0.15 micron for about 8 hours. The example's temperature is printed "1700-1700 °C"; claim 5 gives about 1920 °C for about 16 hours. Volatile matter goes to a graphite condenser; the neodymium stays behind as carbide.
Необходимые инструменты:
Индукционная печь
Вакуумный насос
Графитовый тигель3
3
Purge at 1600 °C
Purge at 1600 °C
Reheat the carbide residue in a carbon crucible at 1600 °C and 0.05 micron for 1 hour (in the example this drove off the last samarium). The residue is substantially pure neodymium carbide.
Необходимые инструменты:
Индукционная печьВакуумный насосГрафитовый тигель4
4
Distil the metal at 1900 °C onto tantalum
Distil the metal at 1900 °C onto tantalum
Heat it in a graphite crucible to 1900 °C at 0.05 micron for 3 hours. Neodymium boils off and condenses on a tantalum plate, which barely alloys with it: 99.21 % neodymium, 0.83 % carbon.
Необходимые инструменты:
Индукционная печьВакуумный насосГрафитовый тигель
Танталовая конденсаторная пластинаМатериалы
2- 78 partsЗаполнитель
- 22 partsЗаполнитель
Требуемые инструменты
6- Заполнитель
- Заполнитель
- Заполнитель
- 1 vendor sell this, none ship to you yetЗаполнитель
- Заполнитель
- Заполнитель
По этому чертежу делают
Связанные чертежи
Эти чертежи делятся знаниями — техники, материалы или принципы
CC0 Общественное достояние
Этот чертёж выпущен под лицензией CC0. Вы можете свободно копировать, изменять, распространять и использовать эту работу в любых целях без запроса разрешения.
Поддержите мейкера, покупая товары через его чертёж, где он получает Комиссию мейкера установленную продавцами, или создайте новую итерацию этого чертежа и включите его как связь в свой чертёж для распределения дохода.