Oriented Barium Ferrite Disc Magnet: Water Instead of a Binder (Gorter, Philips 1956, Ex. 5)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Создано

Charlie

28. октябрь 2026DE
9
0
0
0
0

Oriented Barium Ferrite Disc Magnet: Water Instead of a Binder (Gorter, Philips 1956, Ex. 5)

A ceramic magnet from pre-fired barium ferrite powder stirred into water, oriented in a magnetic field in the die, moulded into blocks and fired as in Example 4. In the principal direction it held 2,870 gauss with a coercive force of 1,610 oersted and a (BH)max of 1.57 × 10⁶; at right angles 1,625 gauss. Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 5. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Продвинутый
3 days

Инструкции

1

Weigh barium carbonate and iron oxide

Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Материалы для этого шага:

Карбонат бария (витерит)Карбонат бария (витерит)450 г
Оксид железа(III)Оксид железа(III)2000 г

Необходимые инструменты:

Рычажные весыРычажные весы
Резиновые перчаткиРезиновые перчатки
Респиратор P100Респиратор P100
2

Mill 20 hours under alcohol, dry

Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.

Необходимые инструменты:

Железная шаровая мельницаЖелезная шаровая мельница
Этанол - лабораторной чистоты, 95 %Этанол - лабораторной чистоты, 95 %
Сушильная печьСушильная печь
3

Pre-fire: through a 1100 °C zone in 10 minutes

Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.

Необходимые инструменты:

Трубчатая печьТрубчатая печь
Тигель с крышкой (фарфоровый)Тигель с крышкой (фарфоровый)
Термостойкие перчаткиТермостойкие перчатки
4

Grind 12 hours with alcohol, dry

Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.

Необходимые инструменты:

Железная шаровая мельницаЖелезная шаровая мельница
Этанол - лабораторной чистоты, 95 %Этанол - лабораторной чистоты, 95 %
Сушильная печьСушильная печь
5

Stir into water

Stir the pre-fired powder with water, 2 cc of water per gram of powder.

Необходимые инструменты:

Дистиллированная водаДистиллированная вода
6

Orient in a first field and mould

Put the suspension in a moulding die, apply a first magnetic field and mould it into blocks. The patent does not give this field's strength.

Необходимые инструменты:

Пресс-форма для дисковПресс-форма для дисков
ЭлектромагнитЭлектромагнит
Гидравлический прессГидравлический пресс
7

Heat to 500 °C in a 2000 oersted field

Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.

Необходимые инструменты:

Трубчатая печьТрубчатая печь
ЭлектромагнитЭлектромагнит
Термостойкие перчаткиТермостойкие перчатки
8

Sinter: through a 1280 °C zone in 5 minutes

Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.

Необходимые инструменты:

Трубчатая печьТрубчатая печь
Термостойкие перчаткиТермостойкие перчатки
9

Magnetise in the principal direction

Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.

Необходимые инструменты:

ЭлектромагнитЭлектромагнит
КомпасКомпас

Материалы

2

Требуемые инструменты

14

По этому чертежу делают

Thumbnail
Заполнитель

Дисковый магнит

Free

11
0
1

Связанные чертежи

Эти чертежи делятся знаниями — техники, материалы или принципы

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

от CharlieDE

Промышленный

11
0
0
0
0
0

CC0 Общественное достояние

Этот чертёж выпущен под лицензией CC0. Вы можете свободно копировать, изменять, распространять и использовать эту работу в любых целях без запроса разрешения.

Поддержите мейкера, покупая товары через его чертёж, где он получает Комиссию мейкера установленную продавцами, или создайте новую итерацию этого чертежа и включите его как связь в свой чертёж для распределения дохода.

Обсуждение

(0)

Войти чтобы присоединиться к обсуждению

Загрузка комментариев...