Oriented Strontium Ferrite Disc Magnet: Less Iron Oxide, 10,000 Oersted Field (Gorter, Philips 1956, Ex. 9)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Создано

Charlie

28. октябрь 2026DE
8
0
0
0
0

Oriented Strontium Ferrite Disc Magnet: Less Iron Oxide, 10,000 Oersted Field (Gorter, Philips 1956, Ex. 9)

A strontium ferrite magnet with less iron oxide than Example 8, oriented, heated and sintered as in Example 4. In the principal direction it held 2,700 gauss with a coercive force of 2,900 oersted and a (BH)max of 1.67 × 10⁶. Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 9. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Продвинутый
3 days

Инструкции

1

Weigh strontium carbonate and iron oxide

Weigh 29.5 g strontium carbonate and 163 g ferric oxide.

Материалы для этого шага:

Карбонат стронцияКарбонат стронция29.5 г
Оксид железа(III)Оксид железа(III)163 г

Необходимые инструменты:

Рычажные весыРычажные весы
Респиратор P100Респиратор P100
2

Mill 15 hours with alcohol, dry

Grind in a ball mill with alcohol for 15 hours. Remove the alcohol and dry the powder.

Необходимые инструменты:

Железная шаровая мельницаЖелезная шаровая мельница
Этанол - лабораторной чистоты, 95 %Этанол - лабораторной чистоты, 95 %
Сушильная печьСушильная печь
3

Pre-fire 2 hours at 1000 °C in air

Heat the powder for 2 hours at 1000 °C in an electric furnace in air. Let it cool.

Необходимые инструменты:

Муфельная печьМуфельная печь
Тигель с крышкой (фарфоровый)Тигель с крышкой (фарфоровый)
Щипцы для тигляЩипцы для тигля
Термостойкие перчаткиТермостойкие перчатки
4

Grind 4 hours in an agate centrifugal mill

Grind the cooled material for 4 hours with alcohol in an agate centrifugal mill, then dry it. This is the pre-fired powder. Example 9 does not say how its powder was pre-fired; ours: as in Example 8.

Необходимые инструменты:

Агатовая центробежная мельницаАгатовая центробежная мельница
Этанол - лабораторной чистоты, 95 %Этанол - лабораторной чистоты, 95 %
Сушильная печьСушильная печь
5

Stir into 8 % polyvinyl acetate in acetone

Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.

Необходимые инструменты:

ПоливинилацетатПоливинилацетат
АцетонАцетон
Рычажные весыРычажные весы
6

Orient in a 10000 oersted field

Put the suspension in a moulding die between the poles of a magnet and apply a first field of 10000 oersted. Remove the binder solution while the field is on.

Необходимые инструменты:

Пресс-форма для дисковПресс-форма для дисков
ЭлектромагнитЭлектромагнит
Гидравлический прессГидравлический пресс
7

Heat to 500 °C in a 2000 oersted field

Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.

Необходимые инструменты:

Трубчатая печьТрубчатая печь
ЭлектромагнитЭлектромагнит
Термостойкие перчаткиТермостойкие перчатки
8

Sinter: through a 1280 °C zone in 5 minutes

Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.

Необходимые инструменты:

Трубчатая печьТрубчатая печь
Термостойкие перчаткиТермостойкие перчатки
9

Magnetise in the principal direction

Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.

Необходимые инструменты:

ЭлектромагнитЭлектромагнит
КомпасКомпас

Материалы

2

Требуемые инструменты

17

По этому чертежу делают

Thumbnail
Заполнитель

Дисковый магнит

Free

11
0
1

Связанные чертежи

Эти чертежи делятся знаниями — техники, материалы или принципы

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

от CharlieDE

Материалы

11
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

от CharlieDE

Органический

14
0
0
0
0
0

CC0 Общественное достояние

Этот чертёж выпущен под лицензией CC0. Вы можете свободно копировать, изменять, распространять и использовать эту работу в любых целях без запроса разрешения.

Поддержите мейкера, покупая товары через его чертёж, где он получает Комиссию мейкера установленную продавцами, или создайте новую итерацию этого чертежа и включите его как связь в свой чертёж для распределения дохода.

Обсуждение

(0)

Войти чтобы присоединиться к обсуждению

Загрузка комментариев...