Metal Oxide Varistor: Zinc Oxide with 12 % Manganese Dioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
A varistor with bismuth oxide fired on from a paste instead of mixed in: 88 % zinc oxide with 12 % manganese dioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 450 at 1 mA and a nonlinearity exponent n of 2.6.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 5. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Продвинутый
2 days
Инструкции
1
1
Weigh 88 : 12 and wet-mill 5 hours
Weigh 88 : 12 and wet-mill 5 hours
Mix zinc oxide and manganese dioxide 88 : 12 by moles. Ours, for 10 g: 8.728 g zinc oxide and 1.272 g manganese dioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Материалы для этого шага:
Порошок оксида цинка8.728 г
Диоксид марганца (пиролюзит)1.272 гНеобходимые инструменты:
Рычажные весы
Железная шаровая мельница
Сушильная печь2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Необходимые инструменты:
Гидравлический пресс
Пресс-форма для дисков
Штангенциркуль3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
As in Example 2: sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Необходимые инструменты:
Муфельная печь4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 5 gives no thickness.
Необходимые инструменты:
Порошок карбида кремнияШтангенциркуль5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Материалы для этого шага:
Оксид висмута1 as requiredНеобходимые инструменты:
Эпоксидная смола
н-БутанолМуфельная печь6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Материалы для этого шага:
Алюминиевый слиток1 as 3.2 mm spray wire
Серебряная токопроводящая краска1 as required
Медная проволока2 штукНеобходимые инструменты:
Штангенциркуль
Электродуговой металлизатор
Промышленный воздушный компрессорМатериалы
6- 8.728 гЗаполнитель
- 1.272 гЗаполнитель
- 1 as requiredЗаполнитель
- 1 as 3.2 mm spray wireЗаполнитель
- 1 as requiredЗаполнитель
- 2 штукЗаполнитель
Требуемые инструменты
12- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
- Заполнитель
По этому чертежу делают
Связанные чертежи
Эти чертежи делятся знаниями — техники, материалы или принципы
CC0 Общественное достояние
Этот чертёж выпущен под лицензией CC0. Вы можете свободно копировать, изменять, распространять и использовать эту работу в любых целях без запроса разрешения.
Поддержите мейкера, покупая товары через его чертёж, где он получает Комиссию мейкера установленную продавцами, или создайте новую итерацию этого чертежа и включите его как связь в свой чертёж для распределения дохода.